- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.917
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
Secant Modulus, MD | 0.160 GPa | 23.2 ksi | ASTM D882 |
Secant Modulus, TD | 0.190 GPa | 27.6 ksi | ASTM D882 |
Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
Elmendorf Tear Strength, MD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
Elmendorf Tear Strength, TD | 24.0 g/micron | 610 g/mil | ASTM D1922 |
Dart Drop | 18.0 g/micron | 457 g/mil | ASTM D1709A |
Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |