- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.916
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.916 g/cc | 0.0331 lb/in³ | |
Melt Flow | 1.0 g/10 min @Load 2.16 kg | 1.0 g/10 min @Load 4.76 lb | |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 11.3 MPa | 1640 psi | |
Film Tensile Strength at Yield, TD | 11.2 MPa | 1620 psi | |
Film Elongation at Break, MD | 635 % | 635 % | |
Film Elongation at Break, TD | 662 % | 662 % | |
Secant Modulus, MD | 0.171 GPa | 24.8 ksi | Film value |
Secant Modulus, TD | 0.1825 GPa | 26.47 ksi | Film value |
Elmendorf Tear Strength MD | 630 g | 630 g | Unspecified film thickness |
Elmendorf Tear Strength TD | 770 g | 770 g | Unspecified film thickness |
Dart drop Test | >= 830 g | >= 1.83 lb | |
Film Tensile Strength at Break, MD | 53.9 MPa | 7820 psi | |
Film Tensile Strength at Break, TD | 51.7 MPa | 7500 psi | |
Thermal Properties | Metric | English | Comments |
Vicat Softening Point | 102 °C | 216 °F | |
Optical Properties | Metric | English | Comments |
Haze | 9.5 % | 9.5 % | |
Processing Properties | Metric | English | Comments |
Processing Temperature | 90.0 °C | 194 °F | Seal Initiation temperature |