- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | |
| Melt Flow | 0.85 g/10 min @Load 2.16 kg | 0.85 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 14.0 MPa | 2030 psi | |
| Film Tensile Strength at Yield, TD | 15.0 MPa | 2180 psi | |
| Film Elongation at Break, MD | 615 % | 615 % | |
| Film Elongation at Break, TD | 640 % | 640 % | |
| Secant Modulus, MD | 0.228 GPa | 33.1 ksi | Film value |
| Secant Modulus, TD | 0.2485 GPa | 36.04 ksi | Film value |
| Elmendorf Tear Strength MD | 750 g | 750 g | Unspecified film thickness |
| Elmendorf Tear Strength TD | 1150 g | 1150 g | Unspecified film thickness |
| Dart drop Test | 400 g | 0.882 lb | |
| Film Tensile Strength at Break, MD | 51.4 MPa | 7450 psi | |
| Film Tensile Strength at Break, TD | 44.5 MPa | 6450 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 113 °C | 235 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 111 °C | 232 °F | Seal Initiation temperature |