- 熔体流动速率 [g/10min]: 85.0
- 密度 [g/cm3]: 0.926
- 缺口冲击强度: 39.0
- 拉伸强度 [MPa]: 9.6
- 弯曲强度 [MPa]: 8.55
- 弯曲模量 [MPa]: 0.356
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | |
| Viscosity | 22000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 22000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 33000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 33000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 39000 cP @Shear Rate 300 1/s, Temperature 190 °C | 39000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 85 g/10 min @Load 2.16 kg | 85 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 6.4. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 8.55 MPa | 1240 psi | |
| Tensile Strength, Yield | 9.60 MPa | 1390 psi | |
| Elongation at Break | 640 % | 640 % | |
| Modulus of Elasticity | 0.219 GPa | 31.8 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.356 GPa | 51.6 ksi | |
| Izod Impact, Notched (ISO) | 39.0 kJ/m² @Temperature -50.0 °C | 18.6 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C | 199 °F | |