- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.917
- 缺口冲击强度: 61.0
- 拉伸强度 [MPa]: 7.3
- 弯曲强度 [MPa]: 11.1
- 弯曲模量 [MPa]: 0.317
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | |
| Viscosity | 47000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 47000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 86000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 86000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 110000 cP @Shear Rate 300 1/s, Temperature 190 °C | 110000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 25 g/10 min @Load 2.16 kg | 25 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.3. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 11.1 MPa | 1610 psi | |
| Tensile Strength, Yield | 7.30 MPa | 1060 psi | |
| Elongation at Break | 650 % | 650 % | |
| Modulus of Elasticity | 0.150 GPa | 21.8 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.317 GPa | 46.0 ksi | |
| Izod Impact, Notched (ISO) | 61.0 kJ/m² @Temperature -50.0 °C | 29.0 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 88.0 °C | 190 °F | |