- 熔体流动速率 [g/10min]: 150.0
- 密度 [g/cm3]: 0.93
- 缺口冲击强度: 29.4
- 拉伸强度 [MPa]: 10.5
- 弯曲强度 [MPa]: 8.6
- 弯曲模量 [MPa]: 0.455
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | |
| Viscosity | 23000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 23000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 50000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 50000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 77000 cP @Shear Rate 300 1/s, Temperature 190 °C | 77000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 150 g/10 min @Load 2.16 kg | 150 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 6.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 8.60 MPa | 1250 psi | |
| Tensile Strength, Yield | 10.5 MPa | 1520 psi | |
| Elongation at Break | 460 % | 460 % | |
| Modulus of Elasticity | 0.268 GPa | 38.9 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.455 GPa | 66.0 ksi | |
| Izod Impact, Notched (ISO) | 29.4 kJ/m² @Temperature -50.0 °C | 14.0 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 96.0 °C | 205 °F | |