- 熔体流动速率 [g/10min]: 1.4
- 密度 [g/cm3]: 0.921
- 脆化温度 [℃]: -70.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
Melt Flow | 1.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
Film Elongation at Break, MD | 640 % | 640 % | ASTM D882 |
Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 |
Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
Secant Modulus, TD | 0.250 GPa | 36.3 ksi | ASTM D882 |
Coefficient of Friction | >= 0.50 | >= 0.50 | ASTM D1894 |
Elmendorf Tear Strength, MD | 5.00 g/micron | 127 g/mil | ASTM D1922 |
Elmendorf Tear Strength, TD | 14.0 g/micron | 356 g/mil | ASTM D1922 |
Dart Drop | 2.00 g/micron | 50.8 g/mil | F 50; ASTM D1709/A |
Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Thermal Properties | Metric | English | Comments |
Vicat Softening Point | 84.0 °C | 183 °F | ASTM D1525 |
Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
Optical Properties | Metric | English | Comments |
Haze | 8.0 % @Thickness 0.0250 mm | 8.0 % @Thickness 0.000984 in | ASTM D1003 |
Gloss | 57 % | 57 % | 45°; 1 mil; ASTM D1894 |
Processing Properties | Metric | English | Comments |
Melt Temperature | 220 - 230 °C | 428 - 446 °F |