- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.919
- 缺口冲击强度: 97.0
- 拉伸强度 [MPa]: 8.1
- 弯曲强度 [MPa]: 12.7
- 弯曲模量 [MPa]: 0.327
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | |
| Viscosity | 82000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 82000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 180000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 180000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 300000 cP @Shear Rate 300 1/s, Temperature 190 °C | 300000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg | 6.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 12.7 MPa | 1840 psi | |
| Tensile Strength, Yield | 8.10 MPa | 1170 psi | |
| Elongation at Break | 560 % | 560 % | |
| Modulus of Elasticity | 0.174 GPa | 25.2 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.327 GPa | 47.4 ksi | |
| Izod Impact, Notched (ISO) | 97.0 kJ/m² @Temperature -50.0 °C | 46.2 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | |