- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 | ||
| Slip Level | 400 ppm | 400 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.10 MPa | 1320 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 8.76 MPa | 1270 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 570 % | 570 % | ASTM D882 | ||
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 | ||
| Puncture Energy | 1.36 J | 1.00 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 0.984 g/micron | 25.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 9.350 g/micron | 237.5 g/mil | ASTM D1922 | ||
| Dart Drop | <= 2.46 g/micron | <= 62.5 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 45.8 MPa | 6640 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 24.3 MPa | 3520 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 166 MPa | 24100 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 172 MPa | 25000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 122 °C | 252 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 110 °C | 230 °F | ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.4 % | 1.4 % | ASTM D1003 | ||
| Gloss | 90 % | 90 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.