- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 12.4
- 弯曲模量 [MPa]: 0.407
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | 180 hour | 180 hour | Condition B, 10%; ASTM D1693 | ||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C | 12 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D638 | ||
| Elongation at Break | 750 % | 750 % | ASTM D638 | ||
| Flexural Modulus | 0.407 GPa | 59.0 ksi | 2% secant; ASTM D790 | ||
| Flexural Modulus, 1% Secant | 455 MPa | 66000 psi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | ASTM D3418 | ||
| Vicat Softening Point | 96.7 °C | 206 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Standard processing antioxidants | ||||
| Form | PELLET | ||||