- 熔体流动速率 [g/10min]: 35.0
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.250
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D4883 |
| Environmental Stress Crack Resistance | <= 1.0 hour | <= 1.0 hour | Condition B, 10%; ASTM D1693 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 190 °C | 35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 11.00 MPa | 1595 psi | ASTM D638 |
| Elongation at Break | 116 % | 116 % | ASTM D638 |
| Flexural Modulus | 0.250 GPa | 36.2 ksi | 1% secant; ASTM D790 |
| Tensile Impact Strength | 233 kJ/m² | 111 ft-lb/in² | at -40°C; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | ASTM D3418 |
| Crystallization Temperature | 106 °C | 223 °F | ASTM D3418 |
| Vicat Softening Point | 92.2 °C | 198 °F | ASTM D1525 |
| Brittleness Temperature | >= -70.0 °C | >= -94.0 °F | ASTM D746 |