- 熔体流动速率 [g/10min]: 3.65
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 3.65 g/10 min | 3.65 g/10 min | ASTM D1238 | ||
| Antiblock Level | 7500 ppm | 7500 ppm | |||
| Slip Level | 1500 ppm | 1500 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.34 MPa | 1210 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 8.07 MPa | 1170 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 530 % | 530 % | ASTM D882 | ||
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 | ||
| Puncture Energy | 0.452 J | 0.333 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 1.48 g/micron | 37.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 10.33 g/micron | 262.5 g/mil | ASTM D1922 | ||
| Dart Drop | <= 2.46 g/micron | <= 62.5 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 39.2 MPa | 5690 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 154 MPa | 22400 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 153.4 MPa | 22250 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.4 % | 5.4 % | ASTM D1003 | ||
| Gloss | 81 % | 81 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.