- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.41 MPa | 1220 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.72 MPa | 1120 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 340 % | 340 % | ASTM D882 | ||
| Film Elongation at Break, TD | 790 % | 790 % | ASTM D882 | ||
| Puncture Energy | 3.28 J | 2.42 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 11.8 g/micron | 300 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 29.53 g/micron | 750.0 g/mil | ASTM D1922 | ||
| Dart Drop | 3.15 g/micron | 80.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 66.1 MPa | 9590 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 38.2 MPa | 5540 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 119 MPa | 17300 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 145 MPa | 21000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.2 % | 2.2 % | ASTM D1003 | ||
| Gloss | 89 % | 89 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||