- 熔体流动速率 [g/10min]: 6.8
- 密度 [g/cm3]: 0.936
- 拉伸强度 [MPa]: 17.2
- 弯曲模量 [MPa]: 0.641
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | 240 hour | 240 hour | Condition B, 10%; ASTM D1693 | ||
| Melt Flow | 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 17.2 MPa | 2500 psi | ASTM D638 | ||
| Elongation at Break | 1100 % | 1100 % | ASTM D638 | ||
| Flexural Modulus | 0.641 GPa | 93.0 ksi | 2% secant; ASTM D790 | ||
| Flexural Modulus, 1% Secant | 758 MPa | 110000 psi | Product Description: LL 6407 is a narrow molecular | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 128 °C | 262 °F | ASTM D3418 | ||
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | antioxidant thermal protection | ||||
| Form | PELLET | ||||