- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 | ||
| Antiblock Level | 9000 ppm | 9000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.31 MPa | 1350 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 | ||
| Film Elongation at Break, TD | 840 % | 840 % | ASTM D882 | ||
| Puncture Energy | 3.05 J | 2.25 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 17.3 g/micron | 440 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 29.1 g/micron | 740 g/mil | ASTM D1922 | ||
| Dart Drop | 5.51 g/micron | 140 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 57.9 MPa | 8400 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 48.1 MPa | 6980 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 197 MPa | 28600 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 238 MPa | 34500 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 256 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 14.9 % | 14.9 % | ASTM D1003 | ||
| Gloss | 49 % | 49 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.