- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 15.2 microns | 0.600 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.1 MPa | 1460 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.50 MPa | 1230 psi | ASTM D882 |
| Film Elongation at Break, MD | 530 % | 530 % | ASTM D882 |
| Film Elongation at Break, TD | 710 % | 710 % | ASTM D882 |
| Secant Modulus, MD | 0.193 GPa | 28.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.221 GPa | 32.1 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 170 g | 170 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 11.1 g/micron | 283 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 32.8 g/micron | 833 g/mil | ASTM D1922 |
| Dart Drop | 7.20 g/micron | 183 g/mil | F50; ASTM D1709 |
| Dart drop Test | 110 g | 0.243 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 57.8 MPa | 8380 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 41.9 MPa | 6080 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 51 % | 51 % | 45°, ASTM D-2457 |