- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | Exxon Method |
| Thickness | 15.2 microns | 0.600 mil | |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.4 MPa | 1800 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.7 MPa | 1990 psi | ASTM D882 |
| Film Elongation at Break, MD | 480 % | 480 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Secant Modulus, MD | 0.262 GPa | 38.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.324 GPa | 47.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 80 g | 80 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 640 g | 640 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 5.24 g/micron | 133 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 42.01 g/micron | 1067 g/mil | ASTM D1922 |
| Dart Drop | 5.24 g/micron | 133 g/mil | F50; ASTM D1709 |
| Dart drop Test | 80.0 g | 0.176 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 66.2 MPa | 9600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.9 MPa | 6800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°, ASTM D-2457 |