- 熔体流动速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.936
- 拉伸强度 [MPa]: 18.6
- 弯曲模量 [MPa]: 0.689
- 热变形温度 [℃]: 50.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D1505 |
Environmental Stress Crack Resistance | >= 200 hour | >= 200 hour | (10% Igepal), F50; ASTM D1693 |
>= 1000 hour | >= 1000 hour | (100% Igepal), F50; ASTM D1693 | |
Melt Flow | 6.5 g/10 min | 6.5 g/10 min | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 2" (50mm) per min.; ASTM D638 |
Elongation at Yield | 11.8 % | 11.8 % | 2" (50mm) per min.; ASTM D638 |
Flexural Modulus | 0.689 GPa | 100 ksi | 1.3mm per min; ASTM D790 |
Dynatup @ -30°C | 61.0 J @Thickness 3.17 mm | 45.0 ft-lb @Thickness 0.125 in | ARM Std. Low Temp Impact; ARM Std. |
Thermal Properties | Metric | English | Comments |
Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ASTM D648 |