- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | Exxon Method |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.8 g/10 min | 1.8 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.80 MPa | 1420 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.80 MPa | 1420 psi | ASTM D882 |
| Film Elongation at Break, MD | 480 % | 480 % | ASTM D882 |
| Film Elongation at Break, TD | 790 % | 790 % | ASTM D882 |
| Secant Modulus, MD | 0.214 GPa | 31.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.248 GPa | 36.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 90 g | 90 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 620 g | 620 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.45 g/micron | 113 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 30.5 g/micron | 775 g/mil | ASTM D1922 |
| Dart Drop | 3.46 g/micron | 88.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 70.0 g | 0.154 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 71.0 MPa | 10300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 36.3 MPa | 5260 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Gloss | 88 % | 88 % | 45°, ASTM D-2457 |