- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 1.8 g/10 min | 1.8 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.6 MPa | 1830 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.6 MPa | 1970 psi | ASTM D882 |
| Film Elongation at Break, MD | 630 % | 630 % | ASTM D882 |
| Film Elongation at Break, TD | 790 % | 790 % | ASTM D882 |
| Secant Modulus, MD | 0.303 GPa | 43.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.338 GPa | 49.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 130 g | 130 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 520 g | 520 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.25 g/micron | 108 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 17.0 g/micron | 433 g/mil | ASTM D1922 |
| Dart Drop | 3.46 g/micron | 88.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 105 g | 0.232 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 55.2 MPa | 8010 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 47 % | 47 % | 45°, ASTM D-2457 |