- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.70 MPa | 1410 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1490 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 750 % | 750 % | ASTM D882 |
| Secant Modulus, MD | 0.207 GPa | 30.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.262 GPa | 38.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 250 g | 250 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 680 g | 680 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.19 g/micron | 208 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.3 g/micron | 567 g/mil | ASTM D1922 |
| Dart Drop | 3.94 g/micron | 100 g/mil | F50; ASTM D1709 |
| Dart drop Test | 120 g | 0.265 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 52.1 MPa | 7560 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.9 MPa | 5500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | ASTM D1003 |
| Gloss | 53 % | 53 % | 45°, ASTM D-2457 |