- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.942
- 拉伸强度 [MPa]: 21.4
- 弯曲模量 [MPa]: 0.827
- 热变形温度 [℃]: 62.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | Condition A, F50; ASTM D1693 |
| ESCR 10% Igepal® | 500 hour | 500 hour | Condition A, F50; ASTM D1693 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | 2" (50mm) per min; ASTM D638 |
| Elongation at Yield | >= 11 % | >= 11 % | 2" (50mm) per min; ASTM D638 |
| Flexural Modulus | 0.827 GPa | 120 ksi | 1.3mm per min; ASTM D790 |
| Impact Test | 81.3 J @Thickness 3.17 mm, Temperature -40.0 °C | 60.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | Low Temperature; ARM |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 °C | 144 °F | ASTM D648 |