- 熔体流动速率 [g/10min]: 34.0
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 22.0
- 弯曲强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Viscosity | 42 cP @Shear Rate 5000 1/s, Temperature 230 °C | 42 cP @Shear Rate 5000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 |
| 73 cP @Shear Rate 1000 1/s, Temperature 230 °C | 73 cP @Shear Rate 1000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| 102 cP @Shear Rate 300 1/s, Temperature 230 °C | 102 cP @Shear Rate 300 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| Melt Flow | 34 g/10 min | 34 g/10 min | Melt Flow Ratio (I10/I2) is 7.3; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Modulus of Elasticity | 1.262 GPa | 183.0 ksi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 121 °C | 250 °F | ASTM D1525 |