- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 724 % | 724 % | ASTM D882 |
| Film Elongation at Break, TD | >= 769 % | >= 769 % | ASTM D882 |
| Secant Modulus, MD | 0.717 GPa | 104 ksi | ASTM D882 |
| Secant Modulus, TD | 0.869 GPa | 126 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 26 g | 26 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 358 g | 358 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 1.02 g/micron | 26.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.1 g/micron | 358 g/mil | ASTM D1922 |
| Dart Drop | 1.93 g/micron | 49.0 g/mil | ASTM D1709 |
| Dart drop Test | 49.0 g | 0.108 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 21 % | 21 % | ASTM D1003 |
| Gloss | 44 % | 44 % | at 45°; ASTM D523 |