- 熔体流动速率 [g/10min]: 6.6
- 密度 [g/cm3]: 0.917
- 弯曲模量 [MPa]: 0.230
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | AT Plastics PTM-03 | ||
| Thickness | >= 10.0 microns | >= 0.394 mil | Coating Thickness | ||
| Melt Flow | 6.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Coating Weight | 9.60 g/m² | 6.00 lb/ream | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 94 | 94 | ASTM D2240 | ||
| Hardness, Shore D | 50 | 50 | ASTM D2240 | ||
| Tensile Strength at Break | 11.0 MPa | 1600 psi | Type IV (50 mm/min); ASTM D638 | ||
| Elongation at Break | 550 % | 550 % | Type IV (50 mm/min); ASTM D638 | ||
| Flexural Modulus | 0.230 GPa | 33.4 ksi | 1% Secant; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 86.0 °C | 187 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Line Speed ft/min | < 700 | ||||