- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 0.937
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 18 % | 18 % | AT Plastics PTM-39 |
| Thickness | 75.0 microns | 2.95 mil | |
| Melt Flow | 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 5.00 MPa | 725 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.00 MPa | 1160 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 440 % | 440 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 590 % | 590 % | Method A (500 mm/min); ASTM D882 |
| Dart Drop | 10.0 g/micron | 254 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | Method A (500 mm/min); ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 88.0 °C | 190 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 62 % | 62 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.1 | 2.1 | |