- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 10.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 - 0.923 g/cc | 0.0333 - 0.0333 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 1.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 - 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 93 | 93 | ASTM D2240 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Elongation at Break | 490 % | 490 % | ASTM D638 |
| Secant Modulus | 0.128 GPa | 18.6 ksi | 5%; ASTM-D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 111 °C | 232 °F | ASTM D3418 |
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 165 - 175 °C | 329 - 347 °F | |
| Mold Temperature | 15.0 - 15.0 °C | 59.0 - 59.0 °F | (close to) |