- 熔体流动速率 [g/10min]: 9.0
- 拉伸强度 [MPa]: 25.5
- 弯曲模量 [MPa]: 0.965
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.949 g/cc | 0.949 g/cc | ASTM D1505 | ||
| Melt Flow | 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 9.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| PENT | >= 10000 hour | >= 10000 hour | ASTM F1473 | ||
| Tensile Strength, Yield | >= 25.5 MPa | >= 3700 psi | 2 in/min, Type IV bar; ASTM D638 | ||
| Elongation at Break | >= 700 % | >= 700 % | 2 in/min, Type IV bar; ASTM D638 | ||
| Flexural Modulus | 0.965 GPa | 140 ksi | 2% Secant; ASTM D790 | ||
| Hydrostatic Design Basis | 6.90 MPa @Temperature 60.0 °C | 1000 psi @Temperature 140 °F | ASTM D2837 | ||
| 11.0 MPa @Temperature 23.0 °C | 1600 psi @Temperature 73.4 °F | ASTM D2837 | |||
| Descriptive Properties | |||||
| Minimum Required Strength | 10.0 MPa | ISO 9080 | |||
| Notched Pipe Test | 500 | ISO 13479, 80°C | |||
| Rapid Crack Propagation | 12 bar | ISO 13477, 0°C | |||