- 熔体流动速率 [g/10min]: 0.06
- 密度 [g/cm3]: 0.961
- 缺口冲击强度: 3.92
- 拉伸强度 [MPa]: 22.6
- 弯曲强度 [MPa]: 29.4
- 弯曲模量 [MPa]: 0.785
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 2000 hour | 2000 hour | ASTM D1693 |
| Carbon Black Loading | 2.0 % | 2.0 % | ASTM D4218 |
| Melt Flow | 0.060 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.060 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 0.40 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.40 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Ultimate | 29.4 MPa | 4270 psi | ASTM D638 |
| Tensile Strength, Yield | 22.6 MPa | 3270 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Flexural Modulus | 0.785 GPa | 114 ksi | Olsen Stiffness; ASTM D747 |
| Izod Impact, Notched | 3.92 J/cm | 7.35 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 262 °F | ASTM D2117 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |