- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.481
- 拉伸强度 [MPa]: 18.8
- 断裂伸长率 [%]: 65.0
- 弯曲强度 [MPa]: 1.35
- 弯曲模量 [MPa]: 1.30
- 硬度: 85.0
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.68 g/cc | 0.0401 - 0.0607 lb/in³ | Average value: 1.38 g/cc Grade Count:693 |
| Filler Content | 20.0 - 35.0 % | 20.0 - 35.0 % | Average value: 30.3 % Grade Count:113 |
| Water Absorption | 0.300 - 6.90 % | 0.300 - 6.90 % | Average value: 2.08 % Grade Count:399 |
| Moisture Absorption at Equilibrium | 0.170 - 5.70 % | 0.170 - 5.70 % | Average value: 1.79 % Grade Count:158 |
| Water Absorption at Saturation | 0.800 - 9.00 % | 0.800 - 9.00 % | Average value: 5.46 % Grade Count:59 |
| Additive Loading | 25.0 - 33.0 % | 25.0 - 33.0 % | Average value: 29.7 % Grade Count:7 |
| Viscosity | 20.0 - 404000 cP @Temperature 270 - 315 °C | 20.0 - 404000 cP @Temperature 518 - 599 °F | Average value: 62800 cP Grade Count:10 |
| 20.0 - 404000 cP @Shear Rate 10.0 - 7000 1/s | 20.0 - 404000 cP @Shear Rate 10.0 - 7000 1/s | Average value: 62800 cP Grade Count:10 | |
| Viscosity Measurement | 0.400 - 160 | 0.400 - 160 | Average value: 108 Grade Count:44 |
| Viscosity Test | 127 - 210 cm³/g | 127 - 210 cm³/g | Average value: 148 cm³/g Grade Count:21 |
| Maximum Moisture Content | 0.0900 - 0.100 | 0.0900 - 0.100 | Average value: 0.0929 Grade Count:7 |
| Linear Mold Shrinkage | 0.000400 - 0.0230 cm/cm | 0.000400 - 0.0230 in/in | Average value: 0.00453 cm/cm Grade Count:550 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.00600 cm/cm | 0.00300 - 0.00600 in/in | Average value: 0.00538 cm/cm Grade Count:13 |
| Linear Mold Shrinkage, Transverse | 0.000500 - 0.0190 cm/cm | 0.000500 - 0.0190 in/in | Average value: 0.00889 cm/cm Grade Count:195 |
| Melt Flow | 1.00 - 198 g/10 min | 1.00 - 198 g/10 min | Average value: 33.2 g/10 min Grade Count:66 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 108 - 113 | 108 - 113 | Average value: 110 Grade Count:6 |
| Hardness, Rockwell M | 53.0 - 104 | 53.0 - 104 | Average value: 88.8 Grade Count:64 |
| Hardness, Rockwell R | 85.0 - 124 | 85.0 - 124 | Average value: 116 Grade Count:177 |
| Hardness, Shore D | 77.0 - 90.0 | 77.0 - 90.0 | Average value: 83.8 Grade Count:9 |
| Ball Indentation Hardness | 125 - 280 MPa | 18100 - 40600 psi | Average value: 205 MPa Grade Count:27 |
| Tensile Strength, Ultimate | 1.35 - 215 MPa | 196 - 31200 psi | Average value: 127 MPa Grade Count:474 |
| 50.0 - 235 MPa @Temperature -40.0 - 150 °C | 7250 - 34100 psi @Temperature -40.0 - 302 °F | Average value: 81.7 MPa Grade Count:12 | |
| 57.5 - 100 MPa @Temperature 130 - 175 °C | 8340 - 14500 psi @Temperature 266 - 347 °F | Average value: 81.7 MPa Grade Count:4 | |
| 57.5 - 100 MPa @Time 1.80e+7 - 7.20e+7 sec | 8340 - 14500 psi @Time 5000 - 20000 hour | Average value: 81.7 MPa Grade Count:4 | |
| 0.640 - 252.178 MPa @Strain 0.000 - 12.5 % | 92.8 - 36575.4 psi @Strain 0.000 - 12.5 % | Average value: 81.7 MPa Grade Count:15 | |
| 0.640 - 252.178 MPa @Temperature -40.0 - 220 °C | 92.8 - 36575.4 psi @Temperature -40.0 - 428 °F | Average value: 81.7 MPa Grade Count:15 | |
| Tensile Strength, Yield | 18.8 - 290 MPa | 2730 - 42100 psi | Average value: 154 MPa Grade Count:236 |
| 231 - 240 MPa @Temperature -40.0 - -40.0 °C | 33500 - 34800 psi @Temperature -40.0 - -40.0 °F | Average value: 236 MPa Grade Count:2 | |
| Elongation at Break | 1.00 - 200 % | 1.00 - 200 % | Average value: 4.14 % Grade Count:601 |
| 2.50 - 11.6 % @Temperature -40.0 - 150 °C | 2.50 - 11.6 % @Temperature -40.0 - 302 °F | Average value: 7.99 % Grade Count:2 | |
| Elongation at Yield | 2.00 - 11.0 % | 2.00 - 11.0 % | Average value: 4.11 % Grade Count:72 |
| Modulus of Elasticity | 1.00 - 84.1 GPa | 145 - 12200 ksi | Average value: 8.56 GPa Grade Count:358 |
| 3.746 - 10.234 GPa @Temperature -40.0 - 150 °C | 543.3 - 1484.3 ksi @Temperature -40.0 - 302 °F | Average value: 6.37 GPa Grade Count:2 | |
| Flexural Yield Strength | 65.0 - 325 MPa | 9430 - 47100 psi | Average value: 226 MPa Grade Count:516 |
| 100 - 315 MPa @Temperature -40.0 - 121 °C | 14500 - 45700 psi @Temperature -40.0 - 250 °F | Average value: 184 MPa Grade Count:9 | |
| Flexural Modulus | 1.30 - 13.5 GPa | 189 - 1960 ksi | Average value: 7.82 GPa Grade Count:585 |
| 1.80 - 10.8 GPa @Temperature -40.0 - 150 °C | 261 - 1570 ksi @Temperature -40.0 - 302 °F | Average value: 4.94 GPa Grade Count:18 | |
| Compressive Yield Strength | 28.0 - 241 MPa | 4060 - 35000 psi | Average value: 145 MPa Grade Count:17 |
| Poissons Ratio | 0.350 - 0.420 | 0.350 - 0.420 | Average value: 0.380 Grade Count:10 |
| Shear Modulus | 1.46 - 3.90 GPa | 212 - 566 ksi | Average value: 2.94 GPa Grade Count:13 |
| 0.209 - 2.26 GPa @Temperature -50.0 - 250 °C | 30.3 - 328 ksi @Temperature -58.0 - 482 °F | Average value: 1.00 GPa Grade Count:3 | |
| Shear Strength | 50.0 - 90.0 MPa | 7250 - 13100 psi | Average value: 77.3 MPa Grade Count:28 |
| Izod Impact, Notched | 0.481 - 75.0 J/cm | 0.900 - 141 ft-lb/in | Average value: 1.37 J/cm Grade Count:372 |
| 0.500 - 3.84408 J/cm @Temperature -40.0 - 149 °C | 0.937 - 7.20154 ft-lb/in @Temperature -40.0 - 300 °F | Average value: 1.17 J/cm Grade Count:10 | |
| 0.64068 - 2.24238 J/cm @Temperature -40.0 - 72.8 °C | 1.2003 - 4.20090 ft-lb/in @Temperature -40.0 - 163 °F | Average value: 1.17 J/cm Grade Count:5 | |
| 0.64068 - 2.24238 J/cm @Thickness 3.17 - 3.17 mm | 1.2003 - 4.20090 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.17 J/cm Grade Count:5 | |
| Izod Impact, Unnotched | 3.20 J/cm - NB | 6.00 ft-lb/in - NB | Average value: 9.06 J/cm Grade Count:73 |
| Izod Impact, Notched (ISO) | 2.50 - 95.0 kJ/m² | 1.19 - 45.2 ft-lb/in² | Average value: 13.4 kJ/m² Grade Count:178 |
| 5.00 - 18.0 kJ/m² @Temperature -40.0 - -20.0 °C | 2.38 - 8.57 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 10.7 kJ/m² Grade Count:50 | |
| Izod Impact, Unnotched (ISO) | 7.00 - 90.0 kJ/m² | 3.33 - 42.8 ft-lb/in² | Average value: 63.3 kJ/m² Grade Count:29 |
| 40.0 - 95.0 kJ/m² @Temperature -30.0 - -30.0 °C | 19.0 - 45.2 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 64.9 kJ/m² Grade Count:21 | |
| Charpy Impact Unnotched | 2.00 J/cm² - NB | 9.52 ft-lb/in² - NB | Average value: 7.03 J/cm² Grade Count:260 |
| 2.00 J/cm² - NB @Temperature -40.0 - 30.0 °C | 9.52 ft-lb/in² - NB @Temperature -40.0 - 86.0 °F | Average value: 5.73 J/cm² Grade Count:128 | |
| 4.20 - 7.00 J/cm² @Temperature 120 - 135 °C | 20.0 - 33.3 ft-lb/in² @Temperature 248 - 275 °F | Average value: 5.73 J/cm² Grade Count:5 | |
| 4.20 - 7.00 J/cm² @Time 720000 - 720000 sec | 20.0 - 33.3 ft-lb/in² @Time 200 - 200 hour | Average value: 5.73 J/cm² Grade Count:5 | |
| Charpy Impact, Notched | 0.250 - 12.0 J/cm² | 1.19 - 57.1 ft-lb/in² | Average value: 1.27 J/cm² Grade Count:273 |
| 0.300 - 18.0 J/cm² @Temperature -40.0 - 30.0 °C | 1.43 - 85.7 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 1.17 J/cm² Grade Count:120 | |
| Puncture Energy | 2.10 - 5.40 J | 1.55 - 3.98 ft-lb | Average value: 3.25 J Grade Count:9 |
| 1.90 - 2.50 J @Temperature -30.0 - -30.0 °C | 1.40 - 1.84 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.06 J Grade Count:8 | |
| 1.90 - 1.90 J @Temperature -30.0 - -30.0 °C | 1.40 - 1.40 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.06 J Grade Count:1 | |
| 1.90 - 1.90 J @Load <=81.6 kg | 1.40 - 1.40 ft-lb @Load <=180 lb | Average value: 2.06 J Grade Count:1 | |
| Coefficient of Friction | 0.150 - 0.500 | 0.150 - 0.500 | Average value: 0.278 Grade Count:12 |
| Coefficient of Friction, Static | 0.140 - 0.230 | 0.140 - 0.230 | Average value: 0.204 Grade Count:10 |
| Tensile Creep Modulus, 1 hour | 0.000 - 9350 MPa | 0.000 - 1.36e+6 psi | Average value: 3240 MPa Grade Count:9 |
| 0.000 - 40.0 MPa @Temperature 80.0 - 100 °C | 0.000 - 5800 psi @Temperature 176 - 212 °F | Average value: 19.5 MPa Grade Count:1 | |
| 0.000 - 40.0 MPa @Strain 0.000 - 0.884 % | 0.000 - 5800 psi @Strain 0.000 - 0.884 % | Average value: 19.5 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 6600 MPa | 0.000 - 957000 psi | Average value: 2590 MPa Grade Count:22 |
| 0.000 - 40.0 MPa @Temperature 80.0 - 100 °C | 0.000 - 5800 psi @Temperature 176 - 212 °F | Average value: 19.5 MPa Grade Count:1 | |
| 0.000 - 40.0 MPa @Strain 0.000 - 0.968 % | 0.000 - 5800 psi @Strain 0.000 - 0.968 % | Average value: 19.5 MPa Grade Count:1 | |
| K (wear) Factor | 36.3 - 604 x 10-8 mm³/N-M | 18.0 - 300 x 10-10 in³-min/ft-lb-hr | Average value: 99.6 x 10-8 mm³/N-M Grade Count:9 |
| Limiting Pressure Velocity | 0.120 - 0.701 MPa-m/sec | 3430 - 20000 psi-ft/min | Average value: 0.578 MPa-m/sec Grade Count:11 |
| Taber Abrasion, mg/1000 Cycles | 12.0 - 20.0 | 12.0 - 20.0 | Average value: 15.6 Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.200 - 1.00e+18 ohm-cm | 0.200 - 1.00e+18 ohm-cm | Average value: 6.33e+15 ohm-cm Grade Count:354 |
| Surface Resistance | 0.0100 - 3.00e+16 ohm | 0.0100 - 3.00e+16 ohm | Average value: 2.94e+14 ohm Grade Count:218 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:7 |
| Dielectric Constant | 2.90 - 12.0 | 2.90 - 12.0 | Average value: 4.41 Grade Count:167 |
| Dielectric Strength | 1.97 - 90.0 kV/mm | 50.0 - 2290 kV/in | Average value: 31.9 kV/mm Grade Count:277 |
| Dissipation Factor | 0.00680 - 0.460 | 0.00680 - 0.460 | Average value: 0.0679 Grade Count:137 |
| Dielectric Loss Index | 0.0140 - 0.150 | 0.0140 - 0.150 | Average value: 0.0707 Grade Count:13 |
| Arc Resistance | 0.000 - 180 sec | 0.000 - 180 sec | Average value: 112 sec Grade Count:19 |
| Comparative Tracking Index | 93.0 - 600 V | 93.0 - 600 V | Average value: 494 V Grade Count:227 |
| Hot Wire Ignition, HWI | 0.000 - 120 sec | 0.000 - 120 sec | Average value: 20.1 sec Grade Count:8 |
| High Amp Arc Ignition, HAI | 0.000 - 120 arcs | 0.000 - 120 arcs | Average value: 97.5 arcs Grade Count:8 |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 150 mm/min | 0.394 - 5.91 in/min | Average value: 72.3 mm/min Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.200 - 500 µm/m-°C | 0.111 - 278 µin/in-°F | Average value: 106 µm/m-°C Grade Count:257 |
| 500 - 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 µin/in-°F @Temperature 131 - 320 °F | Average value: 500 µm/m-°C Grade Count:9 | |
| CTE, linear, Transverse to Flow | 0.600 - 120 µm/m-°C | 0.333 - 66.7 µin/in-°F | Average value: 69.4 µm/m-°C Grade Count:79 |
| 120 - 137 µm/m-°C @Temperature 55.0 - 160 °C | 66.7 - 76.1 µin/in-°F @Temperature 131 - 320 °F | Average value: 131 µm/m-°C Grade Count:9 | |
| Specific Heat Capacity | 0.340 - 2.35 J/g-°C | 0.0813 - 0.562 BTU/lb-°F | Average value: 1.53 J/g-°C Grade Count:24 |
| Thermal Conductivity | 0.216 - 1.60 W/m-K | 1.50 - 11.1 BTU-in/hr-ft²-°F | Average value: 0.367 W/m-K Grade Count:52 |
| Melting Point | 160 - 325 °C | 320 - 617 °F | Average value: 259 °C Grade Count:355 |
| Maximum Service Temperature, Air | 65.0 - 250 °C | 149 - 482 °F | Average value: 166 °C Grade Count:95 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 - 297 °C | 392 - 567 °F | Average value: 254 °C Grade Count:340 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 - 280 °C | 180 - 536 °F | Average value: 242 °C Grade Count:564 |
| Deflection Temperature at 8.0 MPa | 70.0 - 220 °C | 158 - 428 °F | Average value: 136 °C Grade Count:20 |
| Vicat Softening Point | 195 - 258 °C | 383 - 496 °F | Average value: 242 °C Grade Count:104 |
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | Average value: -20.0 °C Grade Count:3 |
| Glass Transition Temp, Tg | 5.00 - 80.0 °C | 41.0 - 176 °F | Average value: 65.8 °C Grade Count:11 |
| Decomposition Temperature | 310 °C | 590 °F | Average value: 310 °C Grade Count:20 |
| UL RTI, Electrical | 65.0 - 160 °C | 149 - 320 °F | Average value: 125 °C Grade Count:37 |
| UL RTI, Mechanical with Impact | 65.0 - 160 °C | 149 - 320 °F | Average value: 109 °C Grade Count:33 |
| UL RTI, Mechanical without Impact | 65.0 - 140 °C | 149 - 284 °F | Average value: 119 °C Grade Count:30 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:419 |
| Oxygen Index | 23.0 - 36.0 % | 23.0 - 36.0 % | Average value: 27.1 % Grade Count:69 |
| Glow Wire Test | 600 - 960 °C | 1110 - 1760 °F | Average value: 813 °C Grade Count:96 |
| Shrinkage | 0.0400 - 0.100 % @Temperature 120 - 120 °C | 0.0400 - 0.100 % @Temperature 248 - 248 °F | Average value: 0.0700 % Grade Count:1 |
| 0.0400 - 0.100 % @Time 14400 - 14400 sec | 0.0400 - 0.100 % @Time 4.00 - 4.00 hour | Average value: 0.0700 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 310 °C | 158 - 590 °F | Average value: 235 °C Grade Count:62 |
| Feed Temperature | 20.0 - 280 °C | 68.0 - 536 °F | Average value: 191 °C Grade Count:56 |
| Nozzle Temperature | 250 - 340 °C | 482 - 644 °F | Average value: 283 °C Grade Count:43 |
| Melt Temperature | 230 - 340 °C | 446 - 644 °F | Average value: 283 °C Grade Count:279 |
| Mold Temperature | 20.0 - 140 °C | 68.0 - 284 °F | Average value: 85.2 °C Grade Count:309 |
| Drying Temperature | 65.6 - 130 °C | 150 - 266 °F | Average value: 81.7 °C Grade Count:221 |
| Dry Time | 1.00 - 12.0 hour | 1.00 - 12.0 hour | Average value: 3.65 hour Grade Count:160 |
| 2.00 - 6.00 hour @Temperature 71.1 - 80.0 °C | 2.00 - 6.00 hour @Temperature 160 - 176 °F | Average value: 3.14 hour Grade Count:14 | |
| Moisture Content | 0.0200 - 2.00 % | 0.0200 - 2.00 % | Average value: 0.192 % Grade Count:187 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -18.6 °C Grade Count:30 |
| Injection Pressure | 4.96 - 140 MPa | 720 - 20300 psi | Average value: 76.3 MPa Grade Count:113 |
| Hold Pressure | 50.0 - 140 MPa | 7250 - 20300 psi | Average value: 83.8 MPa Grade Count:23 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 6.72 MPa Grade Count:50 |
| Clamp Pressure | 26.7 - 97.0 MPa | 3870 - 14100 psi | Average value: 50.6 MPa Grade Count:10 |
| Fill Speed | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Average value: 250 mm/sec Grade Count:3 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 53.3 % Grade Count:15 |
| Cushion | 0.300 - 6.40 cm | 0.118 - 2.52 in | Average value: 0.910 cm Grade Count:10 |
| Screw Speed | 20.0 - 200 rpm | 20.0 - 200 rpm | Average value: 72.6 rpm Grade Count:49 |