- 吸水率 [%]: 0.7
- 成型收缩率 [%]: 0.002
- 缺口冲击强度: 1.175
- 弯曲模量 [MPa]: 9.301
- 硬度: 99.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Water Absorption | 0.70 % @Time 86400 sec | 0.70 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | flow direction; ASTM D955 |
| 0.0050 cm/cm @Thickness 3.17 mm | 0.0050 in/in @Thickness 0.125 in | transverse direction; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength at Break | 199.8 MPa | 28980 psi | ASTM D638 |
| Elongation at Break | 24 % | 24 % | ASTM D638 |
| Flexural Strength | 282.5 MPa | 40970 psi | ASTM D790 |
| Flexural Modulus | 9.301 GPa | 1349 ksi | ASTM D790 |
| Izod Impact, Notched | 1.175 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 2.201 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Tensile Impact Strength | 126.2 kJ/m² | 60.05 ft-lb/in² | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | 0.125";; ASTM D648 |