  4. DuPont Performance Polymers Zytel® 101L NC010 Nylon 66

DuPont Performance Polymers Zytel® 101L NC010 Nylon 66

DuPont Performance Polymers Zytel® 101L NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 101L NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 101L NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 101L NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 1.2
  • 缺口冲击强度: 0.27
  • 拉伸强度 [MPa]: 28.0
  • 弯曲模量 [MPa]: 0.414
  • 硬度: 108.0
  • 热变形温度 [℃]: 200.0
  • 脆化温度 [℃]: -80.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.14 g/cc1.14 g/ccDAM; ASTM D792
Density 1.14 g/cc0.0412 lb/in³DAM; ISO 1183
Water Absorption  1.2 %
@Temperature 23.0 °C		1.2 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 2.6 %
@Temperature 23.0 °C		2.6 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage 0.015 cm/cm
@Thickness 3.20 mm		0.015 in/in
@Thickness 0.126 in		Flow; DAM
Linear Mold Shrinkage, Flow 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 595950%RH; ASTM D785
 595950%RH; ISO 2039/2
 7979DAM; ASTM D785
 7979DAM; ISO 2039/2
Hardness, Rockwell R 10810850%RH; ASTM D785
 10810850%RH; ISO 2039/2
 121121DAM; ASTM D785
 121121DAM; ISO 2039/2
Tensile Strength  38.0 MPa
@Temperature 121 °C		5510 psi
@Temperature 250 °F		50%RH; ASTM D638
 41.0 MPa
@Temperature 77.0 °C		5950 psi
@Temperature 171 °F		50%RH; ASTM D638
 43.0 MPa
@Temperature 121 °C		6240 psi
@Temperature 250 °F		DAM; ASTM D638
 62.0 MPa
@Temperature 77.0 °C		8990 psi
@Temperature 171 °F		DAM; ASTM D638
 77.0 MPa
@Temperature 23.0 °C		11200 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
 110 MPa
@Temperature -40.0 °C		16000 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 114 MPa
@Temperature -40.0 °C		16500 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  10.39 MPa
@Strain 0.390 %,
Temperature 40.0 °C		1507 psi
@Strain 0.390 %,
Temperature 104 °F		DAM; ISO 527
 12.75 MPa
@Strain 0.410 %,
Temperature 23.0 °C		1849 psi
@Strain 0.410 %,
Temperature 73.4 °F		DAM; ISO 527
 14.1 MPa
@Strain 4.76 %,
Temperature 150 °C		2050 psi
@Strain 4.76 %,
Temperature 302 °F		DAM; ISO 527
 14.89 MPa
@Strain 4.60 %,
Temperature 120 °C		2160 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 527
 14.94 MPa
@Strain 4.64 %,
Temperature 120 °C		2167 psi
@Strain 4.64 %,
Temperature 248 °F		DAM; ISO 527
 15.72 MPa
@Strain 0.490 %,
Temperature 0.000 °C		2280 psi
@Strain 0.490 %,
Temperature 32.0 °F		DAM; ISO 527
 16.7 MPa
@Strain 3.43 %,
Temperature 60.0 °C		2420 psi
@Strain 3.43 %,
Temperature 140 °F		50%RH; ISO 527
 17.1 MPa
@Strain 4.23 %,
Temperature 90.0 °C		2480 psi
@Strain 4.23 %,
Temperature 194 °F		50%RH; ISO 527
 17.95 MPa
@Strain 4.64 %,
Temperature 90.0 °C		2603 psi
@Strain 4.64 %,
Temperature 194 °F		DAM; ISO 527
 19.48 MPa
@Strain 3.40 %,
Temperature 40.0 °C		2825 psi
@Strain 3.40 %,
Temperature 104 °F		50%RH; ISO 527
 20.39 MPa
@Strain 9.00 %,
Temperature 120 °C		2957 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 527
 20.57 MPa
@Strain 9.51 %,
Temperature 150 °C		2983 psi
@Strain 9.51 %,
Temperature 302 °F		DAM; ISO 527
 20.88 MPa
@Strain 9.07 %,
Temperature 120 °C		3028 psi
@Strain 9.07 %,
Temperature 248 °F		DAM; ISO 527
 21.07 MPa
@Strain 0.800 %,
Temperature 40.0 °C		3056 psi
@Strain 0.800 %,
Temperature 104 °F		DAM; ISO 527
 22.93 MPa
@Strain 13.4 %,
Temperature 120 °C		3326 psi
@Strain 13.4 %,
Temperature 248 °F		50%RH; ISO 527
 23.28 MPa
@Strain 14.27 %,
Temperature 150 °C		3376 psi
@Strain 14.27 %,
Temperature 302 °F		DAM; ISO 527
 23.82 MPa
@Strain 13.51 %,
Temperature 120 °C		3455 psi
@Strain 13.51 %,
Temperature 248 °F		DAM; ISO 527
 24.04 MPa
@Strain 7.86 %,
Temperature 90.0 °C		3487 psi
@Strain 7.86 %,
Temperature 194 °F		50%RH; ISO 527
 24.34 MPa
@Strain 17.8 %,
Temperature 120 °C		3530 psi
@Strain 17.8 %,
Temperature 248 °F		50%RH; ISO 527
 24.52 MPa
@Strain 4.25 %,
Temperature 60.0 °C		3556 psi
@Strain 4.25 %,
Temperature 140 °F		DAM; ISO 527
 24.67 MPa
@Strain 19.03 %,
Temperature 150 °C		3578 psi
@Strain 19.03 %,
Temperature 302 °F		DAM; ISO 527
 24.73 MPa
@Strain 0.720 %,
Temperature -40.0 °C		3587 psi
@Strain 0.720 %,
Temperature -40.0 °F		DAM; ISO 527
 25.05 MPa
@Strain 8.67 %,
Temperature 90.0 °C		3633 psi
@Strain 8.67 %,
Temperature 194 °F		DAM; ISO 527
 25.31 MPa
@Strain 0.820 %,
Temperature 23.0 °C		3671 psi
@Strain 0.820 %,
Temperature 73.4 °F		DAM; ISO 527
 25.31 MPa
@Strain 22.2 %,
Temperature 120 °C		3671 psi
@Strain 22.2 %,
Temperature 248 °F		50%RH; ISO 527
 25.39 MPa
@Strain 17.54 %,
Temperature 120 °C		3683 psi
@Strain 17.54 %,
Temperature 248 °F		DAM; ISO 527
 25.55 MPa
@Strain 23.78 %,
Temperature 150 °C		3706 psi
@Strain 23.78 %,
Temperature 302 °F		DAM; ISO 527
 26.03 MPa
@Strain 26.6 %,
Temperature 120 °C		3775 psi
@Strain 26.6 %,
Temperature 248 °F		50%RH; ISO 527
 26.16 MPa
@Strain 28.54 %,
Temperature 150 °C		3794 psi
@Strain 28.54 %,
Temperature 302 °F		DAM; ISO 527
 26.24 MPa
@Strain 7.06 %,
Temperature 60.0 °C		3806 psi
@Strain 7.06 %,
Temperature 140 °F		50%RH; ISO 527
 26.57 MPa
@Strain 21.98 %,
Temperature 120 °C		3854 psi
@Strain 21.98 %,
Temperature 248 °F		DAM; ISO 527
 26.57 MPa
@Strain 33.3 %,
Temperature 150 °C		3854 psi
@Strain 33.3 %,
Temperature 302 °F		DAM; ISO 527
 26.61 MPa
@Strain 31.0 %,
Temperature 120 °C		3859 psi
@Strain 31.0 %,
Temperature 248 °F		50%RH; ISO 527
 26.88 MPa
@Strain 38.06 %,
Temperature 150 °C		3899 psi
@Strain 38.06 %,
Temperature 302 °F		DAM; ISO 527
 27.04 MPa
@Strain 35.4 %,
Temperature 120 °C		3922 psi
@Strain 35.4 %,
Temperature 248 °F		50%RH; ISO 527
 27.12 MPa
@Strain 42.81 %,
Temperature 150 °C		3933 psi
@Strain 42.81 %,
Temperature 302 °F		DAM; ISO 527
 27.36 MPa
@Strain 47.57 %,
Temperature 150 °C		3968 psi
@Strain 47.57 %,
Temperature 302 °F		DAM; ISO 527
 27.4 MPa
@Strain 39.8 %,
Temperature 120 °C		3970 psi
@Strain 39.8 %,
Temperature 248 °F		50%RH; ISO 527
 27.4 MPa
@Strain 26.41 %,
Temperature 120 °C		3970 psi
@Strain 26.41 %,
Temperature 248 °F		DAM; ISO 527
 27.65 MPa
@Strain 44.2 %,
Temperature 120 °C		4010 psi
@Strain 44.2 %,
Temperature 248 °F		50%RH; ISO 527
 28.04 MPa
@Strain 30.85 %,
Temperature 120 °C		4067 psi
@Strain 30.85 %,
Temperature 248 °F		DAM; ISO 527
 28.09 MPa
@Strain 11.9 %,
Temperature 90.0 °C		4074 psi
@Strain 11.9 %,
Temperature 194 °F		50%RH; ISO 527
 28.44 MPa
@Strain 3.00 %,
Temperature 23.0 °C		4125 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 527
 28.52 MPa
@Strain 35.28 %,
Temperature 120 °C		4136 psi
@Strain 35.28 %,
Temperature 248 °F		DAM; ISO 527
 28.93 MPa
@Strain 39.72 %,
Temperature 120 °C		4196 psi
@Strain 39.72 %,
Temperature 248 °F		DAM; ISO 527
 29.23 MPa
@Strain 43.75 %,
Temperature 120 °C		4239 psi
@Strain 43.75 %,
Temperature 248 °F		DAM; ISO 527
 29.31 MPa
@Strain 13.11 %,
Temperature 90.0 °C		4251 psi
@Strain 13.11 %,
Temperature 194 °F		DAM; ISO 527
 29.66 MPa
@Strain 1.17 %,
Temperature 40.0 °C		4302 psi
@Strain 1.17 %,
Temperature 104 °F		DAM; ISO 527
 29.9 MPa
@Strain 7.00 %,
Temperature 40.0 °C		4340 psi
@Strain 7.00 %,
Temperature 104 °F		50%RH; ISO 527
 30.08 MPa
@Strain 15.53 %,
Temperature 90.0 °C		4363 psi
@Strain 15.53 %,
Temperature 194 °F		50%RH; ISO 527
 30.47 MPa
@Strain 0.980 %,
Temperature 0.000 °C		4419 psi
@Strain 0.980 %,
Temperature 32.0 °F		DAM; ISO 527
 31.34 MPa
@Strain 10.28 %,
Temperature 60.0 °C		4545 psi
@Strain 10.28 %,
Temperature 140 °F		50%RH; ISO 527
 31.37 MPa
@Strain 19.56 %,
Temperature 90.0 °C		4550 psi
@Strain 19.56 %,
Temperature 194 °F		50%RH; ISO 527
 31.76 MPa
@Strain 17.54 %,
Temperature 90.0 °C		4606 psi
@Strain 17.54 %,
Temperature 194 °F		DAM; ISO 527
 32.08 MPa
@Strain 23.19 %,
Temperature 90.0 °C		4653 psi
@Strain 23.19 %,
Temperature 194 °F		50%RH; ISO 527
 32.58 MPa
@Strain 27.22 %,
Temperature 90.0 °C		4725 psi
@Strain 27.22 %,
Temperature 194 °F		50%RH; ISO 527
 32.92 MPa
@Strain 31.25 %,
Temperature 90.0 °C		4775 psi
@Strain 31.25 %,
Temperature 194 °F		50%RH; ISO 527
 33.06 MPa
@Strain 8.55 %,
Temperature 60.0 °C		4795 psi
@Strain 8.55 %,
Temperature 140 °F		DAM; ISO 527
 33.14 MPa
@Strain 34.88 %,
Temperature 90.0 °C		4807 psi
@Strain 34.88 %,
Temperature 194 °F		50%RH; ISO 527
 33.28 MPa
@Strain 21.98 %,
Temperature 90.0 °C		4827 psi
@Strain 21.98 %,
Temperature 194 °F		DAM; ISO 527
 33.3 MPa
@Strain 38.92 %,
Temperature 90.0 °C		4830 psi
@Strain 38.92 %,
Temperature 194 °F		50%RH; ISO 527
 34.21 MPa
@Strain 26.01 %,
Temperature 90.0 °C		4962 psi
@Strain 26.01 %,
Temperature 194 °F		DAM; ISO 527
 34.48 MPa
@Strain 13.51 %,
Temperature 60.0 °C		5001 psi
@Strain 13.51 %,
Temperature 140 °F		50%RH; ISO 527
 34.93 MPa
@Strain 30.44 %,
Temperature 90.0 °C		5066 psi
@Strain 30.44 %,
Temperature 194 °F		DAM; ISO 527
 35.49 MPa
@Strain 34.88 %,
Temperature 90.0 °C		5147 psi
@Strain 34.88 %,
Temperature 194 °F		DAM; ISO 527
 35.77 MPa
@Strain 10.2 %,
Temperature 40.0 °C		5188 psi
@Strain 10.2 %,
Temperature 104 °F		50%RH; ISO 527
 35.86 MPa
@Strain 39.32 %,
Temperature 90.0 °C		5201 psi
@Strain 39.32 %,
Temperature 194 °F		DAM; ISO 527
 36.03 MPa
@Strain 43.35 %,
Temperature 90.0 °C		5226 psi
@Strain 43.35 %,
Temperature 194 °F		DAM; ISO 527
 36.49 MPa
@Strain 16.73 %,
Temperature 60.0 °C		5292 psi
@Strain 16.73 %,
Temperature 140 °F		50%RH; ISO 527
 37.3 MPa
@Strain 1.24 %,
Temperature 23.0 °C		5410 psi
@Strain 1.24 %,
Temperature 73.4 °F		DAM; ISO 527
 37.34 MPa
@Strain 1.53 %,
Temperature 40.0 °C		5416 psi
@Strain 1.53 %,
Temperature 104 °F		DAM; ISO 527
 37.87 MPa
@Strain 20.36 %,
Temperature 60.0 °C		5493 psi
@Strain 20.36 %,
Temperature 140 °F		50%RH; ISO 527
 38.03 MPa
@Strain 6.20 %,
Temperature 23.0 °C		5516 psi
@Strain 6.20 %,
Temperature 73.4 °F		50%RH; ISO 527
 38.24 MPa
@Strain 12.76 %,
Temperature 60.0 °C		5546 psi
@Strain 12.76 %,
Temperature 140 °F		DAM; ISO 527
 38.6 MPa
@Strain 23.59 %,
Temperature 60.0 °C		5600 psi
@Strain 23.59 %,
Temperature 140 °F		50%RH; ISO 527
 39.04 MPa
@Strain 26.81 %,
Temperature 60.0 °C		5662 psi
@Strain 26.81 %,
Temperature 140 °F		50%RH; ISO 527
 39.27 MPa
@Strain 30.04 %,
Temperature 60.0 °C		5696 psi
@Strain 30.04 %,
Temperature 140 °F		50%RH; ISO 527
 39.4 MPa
@Strain 33.67 %,
Temperature 60.0 °C		5710 psi
@Strain 33.67 %,
Temperature 140 °F		50%RH; ISO 527
 39.6 MPa
@Strain 13.4 %,
Temperature 40.0 °C		5740 psi
@Strain 13.4 %,
Temperature 104 °F		50%RH; ISO 527
 41.57 MPa
@Strain 17.06 %,
Temperature 60.0 °C		6029 psi
@Strain 17.06 %,
Temperature 140 °F		DAM; ISO 527
 42.12 MPa
@Strain 16.6 %,
Temperature 40.0 °C		6109 psi
@Strain 16.6 %,
Temperature 104 °F		50%RH; ISO 527
 43.55 MPa
@Strain 21.26 %,
Temperature 60.0 °C		6316 psi
@Strain 21.26 %,
Temperature 140 °F		DAM; ISO 527
 43.74 MPa
@Strain 9.00 %,
Temperature 23.0 °C		6344 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 527
 43.91 MPa
@Strain 20.2 %,
Temperature 40.0 °C		6369 psi
@Strain 20.2 %,
Temperature 104 °F		50%RH; ISO 527
 44.71 MPa
@Strain 1.94 %,
Temperature 40.0 °C		6485 psi
@Strain 1.94 %,
Temperature 104 °F		DAM; ISO 527
 44.81 MPa
@Strain 25.46 %,
Temperature 60.0 °C		6499 psi
@Strain 25.46 %,
Temperature 140 °F		DAM; ISO 527
 44.88 MPa
@Strain 23.4 %,
Temperature 40.0 °C		6509 psi
@Strain 23.4 %,
Temperature 104 °F		50%RH; ISO 527
 45.2 MPa
@Strain 1.47 %,
Temperature 0.000 °C		6560 psi
@Strain 1.47 %,
Temperature 32.0 °F		DAM; ISO 527
 45.46 MPa
@Strain 26.6 %,
Temperature 40.0 °C		6593 psi
@Strain 26.6 %,
Temperature 104 °F		50%RH; ISO 527
 45.63 MPa
@Strain 29.76 %,
Temperature 60.0 °C		6618 psi
@Strain 29.76 %,
Temperature 140 °F		DAM; ISO 527
 45.79 MPa
@Strain 29.8 %,
Temperature 40.0 °C		6641 psi
@Strain 29.8 %,
Temperature 104 °F		50%RH; ISO 527
 45.98 MPa
@Strain 33.4 %,
Temperature 40.0 °C		6669 psi
@Strain 33.4 %,
Temperature 104 °F		50%RH; ISO 527
 46.19 MPa
@Strain 33.97 %,
Temperature 60.0 °C		6699 psi
@Strain 33.97 %,
Temperature 140 °F		DAM; ISO 527
 46.63 MPa
@Strain 38.27 %,
Temperature 60.0 °C		6763 psi
@Strain 38.27 %,
Temperature 140 °F		DAM; ISO 527
 46.84 MPa
@Strain 1.44 %,
Temperature -40.0 °C		6794 psi
@Strain 1.44 %,
Temperature -40.0 °F		DAM; ISO 527
 46.89 MPa
@Strain 42.47 %,
Temperature 60.0 °C		6801 psi
@Strain 42.47 %,
Temperature 140 °F		DAM; ISO 527
 48.38 MPa
@Strain 12.2 %,
Temperature 23.0 °C		7017 psi
@Strain 12.2 %,
Temperature 73.4 °F		50%RH; ISO 527
 48.64 MPa
@Strain 1.65 %,
Temperature 23.0 °C		7055 psi
@Strain 1.65 %,
Temperature 73.4 °F		DAM; ISO 527
 49.49 MPa
@Strain 2.31 %,
Temperature 40.0 °C		7178 psi
@Strain 2.31 %,
Temperature 104 °F		DAM; ISO 527
 51.21 MPa
@Strain 15.0 %,
Temperature 23.0 °C		7427 psi
@Strain 15.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 52.45 MPa
@Strain 2.67 %,
Temperature 40.0 °C		7607 psi
@Strain 2.67 %,
Temperature 104 °F		DAM; ISO 527
 53.13 MPa
@Strain 17.8 %,
Temperature 23.0 °C		7706 psi
@Strain 17.8 %,
Temperature 73.4 °F		50%RH; ISO 527
 53.95 MPa
@Strain 3.08 %,
Temperature 40.0 °C		7825 psi
@Strain 3.08 %,
Temperature 104 °F		DAM; ISO 527
 54.57 MPa
@Strain 21.0 %,
Temperature 23.0 °C		7915 psi
@Strain 21.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 54.7 MPa
@Strain 3.45 %,
Temperature 40.0 °C		7930 psi
@Strain 3.45 %,
Temperature 104 °F		DAM; ISO 527
 55.31 MPa
@Strain 23.8 %,
Temperature 23.0 °C		8022 psi
@Strain 23.8 %,
Temperature 73.4 °F		50%RH; ISO 527
 55.76 MPa
@Strain 27.0 %,
Temperature 23.0 °C		8087 psi
@Strain 27.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 55.91 MPa
@Strain 29.8 %,
Temperature 23.0 °C		8109 psi
@Strain 29.8 %,
Temperature 73.4 °F		50%RH; ISO 527
 56.3 MPa
@Strain 3.80 %,
Temperature 40.0 °C		8170 psi
@Strain 3.80 %,
Temperature 104 °F		DAM; Yield; ISO 527
 58.52 MPa
@Strain 1.96 %,
Temperature 0.000 °C		8488 psi
@Strain 1.96 %,
Temperature 32.0 °F		DAM; ISO 527
 59.21 MPa
@Strain 2.06 %,
Temperature 23.0 °C		8588 psi
@Strain 2.06 %,
Temperature 73.4 °F		DAM; ISO 527
 66.77 MPa
@Strain 2.16 %,
Temperature -40.0 °C		9684 psi
@Strain 2.16 %,
Temperature -40.0 °F		DAM; ISO 527
 68.16 MPa
@Strain 2.47 %,
Temperature 23.0 °C		9886 psi
@Strain 2.47 %,
Temperature 73.4 °F		DAM; ISO 527
 70.89 MPa
@Strain 2.45 %,
Temperature 0.000 °C		10280 psi
@Strain 2.45 %,
Temperature 32.0 °F		DAM; ISO 527
 75.23 MPa
@Strain 2.89 %,
Temperature 23.0 °C		10910 psi
@Strain 2.89 %,
Temperature 73.4 °F		DAM; ISO 527
 80.02 MPa
@Strain 3.30 %,
Temperature 23.0 °C		11610 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 527
 81.5 MPa
@Strain 2.94 %,
Temperature 0.000 °C		11800 psi
@Strain 2.94 %,
Temperature 32.0 °F		DAM; ISO 527
 82.38 MPa
@Strain 3.71 %,
Temperature 23.0 °C		11950 psi
@Strain 3.71 %,
Temperature 73.4 °F		DAM; ISO 527
 83.33 MPa
@Strain 4.12 %,
Temperature 23.0 °C		12090 psi
@Strain 4.12 %,
Temperature 73.4 °F		DAM; ISO 527
 84.32 MPa
@Strain 2.88 %,
Temperature -40.0 °C		12230 psi
@Strain 2.88 %,
Temperature -40.0 °F		DAM; ISO 527
 89.52 MPa
@Strain 3.43 %,
Temperature 0.000 °C		12980 psi
@Strain 3.43 %,
Temperature 32.0 °F		DAM; ISO 527
 94.79 MPa
@Strain 3.91 %,
Temperature 0.000 °C		13750 psi
@Strain 3.91 %,
Temperature 32.0 °F		DAM; ISO 527
 97.5 MPa
@Strain 4.40 %,
Temperature 0.000 °C		14100 psi
@Strain 4.40 %,
Temperature 32.0 °F		DAM; ISO 527
 98.36 MPa
@Strain 3.60 %,
Temperature -40.0 °C		14270 psi
@Strain 3.60 %,
Temperature -40.0 °F		DAM; ISO 527
 98.47 MPa
@Strain 4.89 %,
Temperature 0.000 °C		14280 psi
@Strain 4.89 %,
Temperature 32.0 °F		DAM; ISO 527
 108.8 MPa
@Strain 4.32 %,
Temperature -40.0 °C		15780 psi
@Strain 4.32 %,
Temperature -40.0 °F		DAM; ISO 527
 115.44 MPa
@Strain 5.04 %,
Temperature -40.0 °C		16743 psi
@Strain 5.04 %,
Temperature -40.0 °F		DAM; ISO 527
 119.27 MPa
@Strain 5.76 %,
Temperature -40.0 °C		17299 psi
@Strain 5.76 %,
Temperature -40.0 °F		DAM; ISO 527
 121.07 MPa
@Strain 6.48 %,
Temperature -40.0 °C		17560 psi
@Strain 6.48 %,
Temperature -40.0 °F		DAM; ISO 527
 121.84 MPa
@Strain 7.20 %,
Temperature -40.0 °C		17671 psi
@Strain 7.20 %,
Temperature -40.0 °F		DAM; ISO 527
Tensile Strength, Yield  28.0 MPa
@Temperature 121 °C		4060 psi
@Temperature 250 °F		50%RH; ASTM D638
 33.0 MPa
@Temperature 121 °C		4790 psi
@Temperature 250 °F		DAM; ASTM D638
 34.0 MPa
@Temperature 77.0 °C		4930 psi
@Temperature 171 °F		50%RH; ASTM D638
 45.0 MPa
@Temperature 77.0 °C		6530 psi
@Temperature 171 °F		DAM; ASTM D638
 55.0 MPa
@Temperature 23.0 °C		7980 psi
@Temperature 73.4 °F		50%RH; ISO 527
 58.0 MPa
@Temperature 23.0 °C		8410 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 82.0 MPa
@Temperature 23.0 °C		11900 psi
@Temperature 73.4 °F		DAM; ISO 527
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
 110 MPa
@Temperature -40.0 °C		16000 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 114 MPa
@Temperature -40.0 °C		16500 psi
@Temperature -40.0 °F		DAM; ASTM D638
Elongation at Break  15 %
@Temperature -40.0 °C		15 %
@Temperature -40.0 °F		DAM; ASTM D638
 20 %
@Temperature -40.0 °C		20 %
@Temperature -40.0 °F		50%RH; ASTM D638
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 45 %
@Temperature 23.0 °C		45 %
@Temperature 73.4 °F		50mm/min; DAM; ISO 527
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 60 %
@Temperature 23.0 °C		60 %
@Temperature 73.4 °F		DAM; ASTM D638
 >= 100 %
@Temperature 23.0 °C		>= 100 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 >= 300 %
@Temperature 23.0 °C		>= 300 %
@Temperature 73.4 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		DAM; ASTM D638
 >= 300 %
@Temperature 121 °C		>= 300 %
@Temperature 250 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 121 °C		>= 300 %
@Temperature 250 °F		DAM; ASTM D638
Elongation at Yield  4.0 %
@Temperature -40.0 °C		4.0 %
@Temperature -40.0 °F		DAM; ASTM D638
 4.5 %
@Temperature 23.0 °C		4.5 %
@Temperature 73.4 °F		DAM; ISO 527
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		50%RH; ASTM D638
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		50%RH; ISO 527
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		50%RH; ASTM D638
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		DAM; ASTM D638
 40 %
@Temperature 121 °C		40 %
@Temperature 250 °F		50%RH; ASTM D638
 45 %
@Temperature 121 °C		45 %
@Temperature 250 °F		DAM; ASTM D638
Tensile Modulus  0.290 GPa
@Temperature 150 °C		42.1 ksi
@Temperature 302 °F		50%RH; ISO 527
 0.373 GPa
@Temperature 120 °C		54.1 ksi
@Temperature 248 °F		50%RH; ISO 527
 0.385 GPa
@Temperature 150 °C		55.8 ksi
@Temperature 302 °F		DAM; ISO 527
 0.460 GPa
@Temperature 120 °C		66.7 ksi
@Temperature 248 °F		DAM; ISO 527
 0.509 GPa
@Temperature 90.0 °C		73.8 ksi
@Temperature 194 °F		50%RH; ISO 527
 0.559 GPa
@Temperature 90.0 °C		81.1 ksi
@Temperature 194 °F		DAM; ISO 527
 0.686 GPa
@Temperature 60.0 °C		99.5 ksi
@Temperature 140 °F		50%RH; ISO 527
 0.945 GPa
@Temperature 40.0 °C		137 ksi
@Temperature 104 °F		50%RH; ISO 527
 1.15 GPa
@Temperature 60.0 °C		167 ksi
@Temperature 140 °F		DAM; ISO 527
 1.40 GPa
@Temperature 23.0 °C		203 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 2.769 GPa
@Temperature 40.0 °C		401.6 ksi
@Temperature 104 °F		DAM; ISO 527
 2.858 GPa
@Temperature 0.000 °C		414.5 ksi
@Temperature 32.0 °F		50%RH; ISO 527
 3.10 GPa
@Temperature 23.0 °C		450 ksi
@Temperature 73.4 °F		DAM; ISO 527
 3.385 GPa
@Temperature 0.000 °C		491.0 ksi
@Temperature 32.0 °F		DAM; ISO 527
 3.418 GPa
@Temperature -20.0 °C		495.7 ksi
@Temperature -4.00 °F		DAM; ISO 527
 3.555 GPa
@Temperature -40.0 °C		515.6 ksi
@Temperature -40.0 °F		DAM; ISO 527
 3.775 GPa
@Temperature -20.0 °C		547.5 ksi
@Temperature -4.00 °F		50%RH; ISO 527
 4.493 GPa
@Temperature -40.0 °C		651.7 ksi
@Temperature -40.0 °F		50%RH; ISO 527
Flexural Modulus  0.414 GPa
@Temperature 121 °C		60.0 ksi
@Temperature 250 °F		50%RH; ASTM D790
 0.538 GPa
@Temperature 121 °C		78.0 ksi
@Temperature 250 °F		DAM; ASTM D790
 0.565 GPa
@Temperature 77.0 °C		81.9 ksi
@Temperature 171 °F		50%RH; ASTM D790
 0.690 GPa
@Temperature 77.0 °C		100 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.20 GPa
@Temperature 23.0 °C		174 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 1.21 GPa
@Temperature 23.0 °C		175 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.80 GPa
@Temperature 23.0 °C		406 ksi
@Temperature 73.4 °F		DAM; ISO 178
 2.83 GPa
@Temperature 23.0 °C		410 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 3.24 GPa
@Temperature -40.0 °C		470 ksi
@Temperature -40.0 °F		DAM; ASTM D790
 3.45 GPa
@Temperature -40.0 °C		500 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
Shear Modulus  0.0430 GPa
@Temperature 250 °C		6.24 ksi
@Temperature 482 °F		50%RH; ISO 6721
 0.0570 GPa
@Temperature 250 °C		8.27 ksi
@Temperature 482 °F		DAM; ISO 6721
 0.0680 GPa
@Temperature 240 °C		9.86 ksi
@Temperature 464 °F		50%RH; ISO 6721
 0.0760 GPa
@Temperature 240 °C		11.0 ksi
@Temperature 464 °F		DAM; ISO 6721
 0.0870 GPa
@Temperature 230 °C		12.6 ksi
@Temperature 446 °F		50%RH; ISO 6721
 0.0960 GPa
@Temperature 230 °C		13.9 ksi
@Temperature 446 °F		DAM; ISO 6721
 0.102 GPa
@Temperature 220 °C		14.8 ksi
@Temperature 428 °F		50%RH; ISO 6721
 0.113 GPa
@Temperature 210 °C		16.4 ksi
@Temperature 410 °F		50%RH; ISO 6721
 0.114 GPa
@Temperature 220 °C		16.5 ksi
@Temperature 428 °F		DAM; ISO 6721
 0.121 GPa
@Temperature 200 °C		17.5 ksi
@Temperature 392 °F		50%RH; ISO 6721
 0.125 GPa
@Temperature 210 °C		18.1 ksi
@Temperature 410 °F		DAM; ISO 6721
 0.127 GPa
@Temperature 190 °C		18.4 ksi
@Temperature 374 °F		50%RH; ISO 6721
 0.133 GPa
@Temperature 180 °C		19.3 ksi
@Temperature 356 °F		50%RH; ISO 6721
 0.134 GPa
@Temperature 200 °C		19.4 ksi
@Temperature 392 °F		DAM; ISO 6721
 0.138 GPa
@Temperature 170 °C		20.0 ksi
@Temperature 338 °F		50%RH; ISO 6721
 0.141 GPa
@Temperature 190 °C		20.5 ksi
@Temperature 374 °F		DAM; ISO 6721
 0.144 GPa
@Temperature 160 °C		20.9 ksi
@Temperature 320 °F		50%RH; ISO 6721
 0.148 GPa
@Temperature 150 °C		21.5 ksi
@Temperature 302 °F		50%RH; ISO 6721
 0.148 GPa
@Temperature 180 °C		21.5 ksi
@Temperature 356 °F		DAM; ISO 6721
 0.153 GPa
@Temperature 140 °C		22.2 ksi
@Temperature 284 °F		50%RH; ISO 6721
 0.154 GPa
@Temperature 170 °C		22.3 ksi
@Temperature 338 °F		DAM; ISO 6721
 0.158 GPa
@Temperature 130 °C		22.9 ksi
@Temperature 266 °F		50%RH; ISO 6721
 0.160 GPa
@Temperature 160 °C		23.2 ksi
@Temperature 320 °F		DAM; ISO 6721
 0.163 GPa
@Temperature 120 °C		23.6 ksi
@Temperature 248 °F		50%RH; ISO 6721
 0.165 GPa
@Temperature 150 °C		23.9 ksi
@Temperature 302 °F		DAM; ISO 6721
 0.170 GPa
@Temperature 140 °C		24.7 ksi
@Temperature 284 °F		DAM; ISO 6721
 0.171 GPa
@Temperature 110 °C		24.8 ksi
@Temperature 230 °F		50%RH; ISO 6721
 0.174 GPa
@Temperature 130 °C		25.2 ksi
@Temperature 266 °F		DAM; ISO 6721
 0.180 GPa
@Temperature 120 °C		26.1 ksi
@Temperature 248 °F		DAM; ISO 6721
 0.184 GPa
@Temperature 100 °C		26.7 ksi
@Temperature 212 °F		50%RH; ISO 6721
 0.186 GPa
@Temperature 110 °C		27.0 ksi
@Temperature 230 °F		DAM; ISO 6721
 0.197 GPa
@Temperature 100 °C		28.6 ksi
@Temperature 212 °F		DAM; ISO 6721
 0.206 GPa
@Temperature 90.0 °C		29.9 ksi
@Temperature 194 °F		50%RH; ISO 6721
 0.218 GPa
@Temperature 90.0 °C		31.6 ksi
@Temperature 194 °F		DAM; ISO 6721
 0.237 GPa
@Temperature 80.0 °C		34.4 ksi
@Temperature 176 °F		50%RH; ISO 6721
 0.258 GPa
@Temperature 80.0 °C		37.4 ksi
@Temperature 176 °F		DAM; ISO 6721
 0.281 GPa
@Temperature 70.0 °C		40.8 ksi
@Temperature 158 °F		50%RH; ISO 6721
 0.335 GPa
@Temperature 70.0 °C		48.6 ksi
@Temperature 158 °F		DAM; ISO 6721
 0.365 GPa
@Temperature 60.0 °C		52.9 ksi
@Temperature 140 °F		50%RH; ISO 6721
 0.474 GPa
@Temperature 60.0 °C		68.7 ksi
@Temperature 140 °F		DAM; ISO 6721
 0.575 GPa
@Temperature 50.0 °C		83.4 ksi
@Temperature 122 °F		50%RH; ISO 6721
 0.683 GPa
@Temperature 50.0 °C		99.1 ksi
@Temperature 122 °F		DAM; ISO 6721
 0.699 GPa
@Temperature 40.0 °C		101 ksi
@Temperature 104 °F		50%RH; ISO 6721
 0.776 GPa
@Temperature 30.0 °C		113 ksi
@Temperature 86.0 °F		50%RH; ISO 6721
 0.802 GPa
@Temperature 40.0 °C		116 ksi
@Temperature 104 °F		DAM; ISO 6721
 0.829 GPa
@Temperature 20.0 °C		120 ksi
@Temperature 68.0 °F		50%RH; ISO 6721
 0.868 GPa
@Temperature 10.0 °C		126 ksi
@Temperature 50.0 °F		50%RH; ISO 6721
 0.872 GPa
@Temperature 30.0 °C		126 ksi
@Temperature 86.0 °F		DAM; ISO 6721
 0.901 GPa
@Temperature 0.000 °C		131 ksi
@Temperature 32.0 °F		50%RH; ISO 6721
 0.919 GPa
@Temperature 20.0 °C		133 ksi
@Temperature 68.0 °F		DAM; ISO 6721
 0.928 GPa
@Temperature -10.0 °C		135 ksi
@Temperature 14.0 °F		50%RH; ISO 6721
 0.944 GPa
@Temperature -20.0 °C		137 ksi
@Temperature -4.00 °F		50%RH; ISO 6721
 0.952 GPa
@Temperature 10.0 °C		138 ksi
@Temperature 50.0 °F		DAM; ISO 6721
 0.959 GPa
@Temperature -30.0 °C		139 ksi
@Temperature -22.0 °F		50%RH; ISO 6721
 0.983 GPa
@Temperature -40.0 °C		143 ksi
@Temperature -40.0 °F		50%RH; ISO 6721
 0.984 GPa
@Temperature 0.000 °C		143 ksi
@Temperature 32.0 °F		DAM; ISO 6721
 1.01 GPa
@Temperature -10.0 °C		146 ksi
@Temperature 14.0 °F		DAM; ISO 6721
 1.02 GPa
@Temperature -20.0 °C		148 ksi
@Temperature -4.00 °F		DAM; ISO 6721
 1.02 GPa
@Temperature -50.0 °C		148 ksi
@Temperature -58.0 °F		50%RH; ISO 6721
 1.04 GPa
@Temperature -30.0 °C		151 ksi
@Temperature -22.0 °F		DAM; ISO 6721
 1.07 GPa
@Temperature -40.0 °C		155 ksi
@Temperature -40.0 °F		DAM; ISO 6721
 1.11 GPa
@Temperature -50.0 °C		161 ksi
@Temperature -58.0 °F		DAM; ISO 6721
Shear Strength 66.0 MPa
@Temperature 23.0 °C		9570 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.270 J/cm
@Temperature -40.0 °C		0.506 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.530 J/cm
@Temperature 23.0 °C		0.993 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.12 J/cm
@Temperature 23.0 °C		2.10 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  3.00 kJ/m²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 5.50 kJ/m²
@Temperature -40.0 °C		2.62 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature -30.0 °C		2.62 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 12.0 kJ/m²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  300 kJ/m²
@Temperature -30.0 °C		143 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 180/1U
Charpy Impact Unnotched  40.0 J/cm²
@Temperature -30.0 °C		190 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.300 J/cm²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.450 J/cm²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.550 J/cm²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.50 J/cm²
@Temperature 23.0 °C		7.14 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Impact Strength  157 kJ/m²
@Temperature 23.0 °C		74.7 ft-lb/in²
@Temperature 73.4 °F		DAM; Short specimen; ASTM D1822
 232 kJ/m²
@Temperature 23.0 °C		110 ft-lb/in²
@Temperature 73.4 °F		50%RH; Short specimen; ASTM D1822
 504 kJ/m²
@Temperature 23.0 °C		240 ft-lb/in²
@Temperature 73.4 °F		DAM; Long specimen; ASTM D1822
 1470 kJ/m²
@Temperature 23.0 °C		699 ft-lb/in²
@Temperature 73.4 °F		50%RH; Long specimen; ASTM D1822
Tensile Creep Modulus, 1 hour 1400 MPa
@Temperature 23.0 °C		203000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.0970 %,
Temperature 60.0 °C		145 psi
@Strain 0.0970 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.111 %,
Temperature 60.0 °C		145 psi
@Strain 0.111 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.302 %,
Temperature 90.0 °C		174 psi
@Strain 0.302 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.262 %,
Temperature 90.0 °C		174 psi
@Strain 0.262 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.157 %,
Temperature 23.0 °C		290 psi
@Strain 0.157 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.202 %,
Temperature 60.0 °C		290 psi
@Strain 0.202 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.230 %,
Temperature 60.0 °C		290 psi
@Strain 0.230 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.135 %,
Temperature 23.0 °C		290 psi
@Strain 0.135 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.609 %,
Temperature 90.0 °C		348 psi
@Strain 0.609 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.529 %,
Temperature 90.0 °C		348 psi
@Strain 0.529 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.807 %,
Temperature 90.0 °C		522 psi
@Strain 0.807 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.927 %,
Temperature 90.0 °C		522 psi
@Strain 0.927 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.500 %,
Temperature 60.0 °C		580 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.284 %,
Temperature 23.0 °C		580 psi
@Strain 0.284 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.332 %,
Temperature 23.0 °C		580 psi
@Strain 0.332 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.437 %,
Temperature 60.0 °C		580 psi
@Strain 0.437 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 4.80 MPa
@Strain 1.10 %,
Temperature 90.0 °C		696 psi
@Strain 1.10 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 4.80 MPa
@Strain 1.26 %,
Temperature 90.0 °C		696 psi
@Strain 1.26 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.62 %,
Temperature 90.0 °C		870 psi
@Strain 1.62 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.812 %,
Temperature 60.0 °C		870 psi
@Strain 0.812 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.42 %,
Temperature 90.0 °C		870 psi
@Strain 1.42 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.707 %,
Temperature 60.0 °C		870 psi
@Strain 0.707 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 7.20 MPa
@Strain 1.77 %,
Temperature 90.0 °C		1040 psi
@Strain 1.77 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 7.20 MPa
@Strain 2.01 %,
Temperature 90.0 °C		1040 psi
@Strain 2.01 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.16 %,
Temperature 60.0 °C		1160 psi
@Strain 1.16 %,
Temperature 140 °F		50%RH; 10h; Break; Isochronous; ISO 899
 8.00 MPa
@Strain 0.626 %,
Temperature 23.0 °C		1160 psi
@Strain 0.626 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.745 %,
Temperature 23.0 °C		1160 psi
@Strain 0.745 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.00 %,
Temperature 60.0 °C		1160 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; 1h; Break; Isochronous; ISO 899
 8.40 MPa
@Strain 2.16 %,
Temperature 90.0 °C		1220 psi
@Strain 2.16 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 8.40 MPa
@Strain 2.43 %,
Temperature 90.0 °C		1220 psi
@Strain 2.43 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 9.60 MPa
@Strain 2.90 %,
Temperature 90.0 °C		1390 psi
@Strain 2.90 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 9.60 MPa
@Strain 2.59 %,
Temperature 90.0 °C		1390 psi
@Strain 2.59 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 10.8 MPa
@Strain 3.08 %,
Temperature 90.0 °C		1570 psi
@Strain 3.08 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 10.8 MPa
@Strain 3.42 %,
Temperature 90.0 °C		1570 psi
@Strain 3.42 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 12.0 MPa
@Strain 4.00 %,
Temperature 90.0 °C		1740 psi
@Strain 4.00 %,
Temperature 194 °F		50%RH; 10h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 1.02 %,
Temperature 23.0 °C		1740 psi
@Strain 1.02 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 12.0 MPa
@Strain 3.63 %,
Temperature 90.0 °C		1740 psi
@Strain 3.63 %,
Temperature 194 °F		50%RH; 1h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 1.25 %,
Temperature 23.0 °C		1740 psi
@Strain 1.25 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 14.0 MPa
@Strain 1.53 %,
Temperature 23.0 °C		2030 psi
@Strain 1.53 %,
Temperature 73.4 °F		50%RH; 10h; Break; Isochronous; ISO 899
 14.0 MPa
@Strain 1.24 %,
Temperature 23.0 °C		2030 psi
@Strain 1.24 %,
Temperature 73.4 °F		50%RH; 1h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 820 MPa
@Temperature 23.0 °C		119000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.151 %,
Temperature 60.0 °C		145 psi
@Strain 0.151 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.142 %,
Temperature 60.0 °C		145 psi
@Strain 0.142 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.129 %,
Temperature 60.0 °C		145 psi
@Strain 0.129 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.401 %,
Temperature 90.0 °C		174 psi
@Strain 0.401 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.457 %,
Temperature 90.0 °C		174 psi
@Strain 0.457 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.348 %,
Temperature 90.0 °C		174 psi
@Strain 0.348 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.305 %,
Temperature 23.0 °C		290 psi
@Strain 0.305 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.294 %,
Temperature 60.0 °C		290 psi
@Strain 0.294 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.239 %,
Temperature 23.0 °C		290 psi
@Strain 0.239 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.269 %,
Temperature 60.0 °C		290 psi
@Strain 0.269 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.192 %,
Temperature 23.0 °C		290 psi
@Strain 0.192 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.314 %,
Temperature 60.0 °C		290 psi
@Strain 0.314 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.807 %,
Temperature 90.0 °C		348 psi
@Strain 0.807 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.917 %,
Temperature 90.0 °C		348 psi
@Strain 0.917 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.701 %,
Temperature 90.0 °C		348 psi
@Strain 0.701 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 3.60 MPa
@Strain 1.06 %,
Temperature 90.0 °C		522 psi
@Strain 1.06 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 3.60 MPa
@Strain 1.39 %,
Temperature 90.0 °C		522 psi
@Strain 1.39 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 3.60 MPa
@Strain 1.22 %,
Temperature 90.0 °C		522 psi
@Strain 1.22 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.408 %,
Temperature 23.0 °C		580 psi
@Strain 0.408 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.586 %,
Temperature 60.0 °C		580 psi
@Strain 0.586 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.506 %,
Temperature 23.0 °C		580 psi
@Strain 0.506 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.633 %,
Temperature 60.0 °C		580 psi
@Strain 0.633 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.646 %,
Temperature 23.0 °C		580 psi
@Strain 0.646 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.667 %,
Temperature 60.0 °C		580 psi
@Strain 0.667 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 4.80 MPa
@Strain 1.44 %,
Temperature 90.0 °C		696 psi
@Strain 1.44 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 4.80 MPa
@Strain 1.87 %,
Temperature 90.0 °C		696 psi
@Strain 1.87 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 4.80 MPa
@Strain 1.65 %,
Temperature 90.0 °C		696 psi
@Strain 1.65 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 2.10 %,
Temperature 90.0 °C		870 psi
@Strain 2.10 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.950 %,
Temperature 60.0 °C		870 psi
@Strain 0.950 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 2.37 %,
Temperature 90.0 °C		870 psi
@Strain 2.37 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.02 %,
Temperature 60.0 °C		870 psi
@Strain 1.02 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.85 %,
Temperature 90.0 °C		870 psi
@Strain 1.85 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.06 %,
Temperature 60.0 °C		870 psi
@Strain 1.06 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 7.20 MPa
@Strain 2.27 %,
Temperature 90.0 °C		1040 psi
@Strain 2.27 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 7.20 MPa
@Strain 2.89 %,
Temperature 90.0 °C		1040 psi
@Strain 2.89 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 7.20 MPa
@Strain 2.58 %,
Temperature 90.0 °C		1040 psi
@Strain 2.58 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.35 %,
Temperature 60.0 °C		1160 psi
@Strain 1.35 %,
Temperature 140 °F		50%RH; 100h; Break; Isochronous; ISO 899
 8.00 MPa
@Strain 0.917 %,
Temperature 23.0 °C		1160 psi
@Strain 0.917 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.44 %,
Temperature 60.0 °C		1160 psi
@Strain 1.44 %,
Temperature 140 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 8.00 MPa
@Strain 1.15 %,
Temperature 23.0 °C		1160 psi
@Strain 1.15 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.46 %,
Temperature 23.0 °C		1160 psi
@Strain 1.46 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.49 %,
Temperature 60.0 °C		1160 psi
@Strain 1.49 %,
Temperature 140 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 8.40 MPa
@Strain 2.74 %,
Temperature 90.0 °C		1220 psi
@Strain 2.74 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 8.40 MPa
@Strain 3.44 %,
Temperature 90.0 °C		1220 psi
@Strain 3.44 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 8.40 MPa
@Strain 3.04 %,
Temperature 90.0 °C		1220 psi
@Strain 3.04 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 9.60 MPa
@Strain 3.63 %,
Temperature 90.0 °C		1390 psi
@Strain 3.63 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 9.60 MPa
@Strain 4.03 %,
Temperature 90.0 °C		1390 psi
@Strain 4.03 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 9.60 MPa
@Strain 3.24 %,
Temperature 90.0 °C		1390 psi
@Strain 3.24 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 10.8 MPa
@Strain 3.80 %,
Temperature 90.0 °C		1570 psi
@Strain 3.80 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 10.8 MPa
@Strain 4.65 %,
Temperature 90.0 °C		1570 psi
@Strain 4.65 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 10.8 MPa
@Strain 4.21 %,
Temperature 90.0 °C		1570 psi
@Strain 4.21 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 4.85 %,
Temperature 90.0 °C		1740 psi
@Strain 4.85 %,
Temperature 194 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 1.52 %,
Temperature 23.0 °C		1740 psi
@Strain 1.52 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 12.0 MPa
@Strain 5.31 %,
Temperature 90.0 °C		1740 psi
@Strain 5.31 %,
Temperature 194 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 1.95 %,
Temperature 23.0 °C		1740 psi
@Strain 1.95 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 4.41 %,
Temperature 90.0 °C		1740 psi
@Strain 4.41 %,
Temperature 194 °F		50%RH; 100h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 2.50 %,
Temperature 23.0 °C		1740 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 14.0 MPa
@Strain 2.42 %,
Temperature 23.0 °C		2030 psi
@Strain 2.42 %,
Temperature 73.4 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 14.0 MPa
@Strain 3.13 %,
Temperature 23.0 °C		2030 psi
@Strain 3.13 %,
Temperature 73.4 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 14.0 MPa
@Strain 1.86 %,
Temperature 23.0 °C		2030 psi
@Strain 1.86 %,
Temperature 73.4 °F		50%RH; 100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+12 ohm-cm
@Temperature 23.0 °C		1.00e+12 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+14 ohm-cm
@Temperature 23.0 °C		1.00e+14 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Surface Resistance  1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		50%RH; IEC 60093
Dielectric Constant  3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.8
@Frequency 100 Hz,
Temperature 23.0 °C		3.8
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.9
@Frequency 1000 Hz,
Temperature 23.0 °C		3.9
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 100 Hz,
Temperature 23.0 °C		4.0
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 4.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 7.0
@Frequency 1000 Hz,
Temperature 23.0 °C		7.0
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 8.0
@Frequency 100 Hz,
Temperature 23.0 °C		8.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 10.9
@Frequency 100 Hz,
Temperature 23.0 °C		10.9
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength 31.5 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		800 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.0080
@Frequency 100 Hz,
Temperature 23.0 °C		0.0080
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.018
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.075
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.075
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.10
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.10
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 100 Hz,
Temperature 23.0 °C		0.20
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 1000 Hz,
Temperature 23.0 °C		0.20
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.21
@Frequency 100 Hz,
Temperature 23.0 °C		0.21
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index  >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; IEC 60112
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 200 °C392 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C149 °FDAM; ASTM D648
 70.0 °C158 °FDAM; ISO 75-1/-2
Brittleness Temperature -80.0 °C-112 °FDAM; ASTM D746
 -65.0 °C-85.0 °F50%RH; ASTM D746
Glass Transition Temp, Tg 60.0 °C140 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 0.400 mm		149 °F
@Thickness 0.0157 in		DAM; UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 0.400 mm		149 °F
@Thickness 0.0157 in		DAM; UL 746B
 75.0 °C
@Thickness 3.00 mm		167 °F
@Thickness 0.118 in		DAM; UL 746B
 75.0 °C
@Thickness 1.50 mm		167 °F
@Thickness 0.0591 in		DAM; UL 746B
 75.0 °C
@Thickness 6.00 mm		167 °F
@Thickness 0.236 in		DAM; UL 746B
 75.0 °C
@Thickness 0.710 mm		167 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 0.400 mm		149 °F
@Thickness 0.0157 in		DAM; UL 746B
 85.0 °C
@Thickness 1.50 mm		185 °F
@Thickness 0.0591 in		DAM; UL 746B
 85.0 °C
@Thickness 6.00 mm		185 °F
@Thickness 0.236 in		DAM; UL 746B
 85.0 °C
@Thickness 3.00 mm		185 °F
@Thickness 0.118 in		DAM; UL 746B
 85.0 °C
@Thickness 0.710 mm		185 °F
@Thickness 0.0280 in		DAM; UL 746B
Flammability, UL94  V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; IEC 60695-11-10
 V-2
@Thickness 0.400 mm		V-2
@Thickness 0.0157 in		DAM; IEC 60695-11-10
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; UL94
 V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; UL94
 V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; UL94
 V-2
@Thickness 0.400 mm		V-2
@Thickness 0.0157 in		DAM; UL94
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; UL94
Oxygen Index 28 %28 %DAM; ASTM D2863
 28 %28 %DAM; ISO 4589-1/-2
 31 %31 %50%RH; ASTM D2863
Glow Wire Test  725 °C
@Thickness 0.710 mm		1340 °F
@Thickness 0.0280 in		DAM; Ignition; IEC 60695-2-13
 750 °C
@Thickness 1.50 mm		1380 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 900 °C
@Thickness 0.400 mm		1650 °F
@Thickness 0.0157 in		DAM; Ignition; IEC 60695-2-13
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 0.710 mm		1760 °F
@Thickness 0.0280 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 0.400 mm		1760 °F
@Thickness 0.0157 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 290 °C554 °FDAM; Optimum
 280 - 300 °C536 - 572 °FDAM
Mold Temperature 70.0 °C158 °FDAM; optimum
 50.0 - 90.0 °C122 - 194 °FDAM
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveLubricantDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesChemical Resistance, GoodDAM
 Cycle (Production), FastDAM
 Electrical Properties, GoodDAM
 Fatigue ResistantDAM
 Flow, HighDAM
 Fuel ResistantDAM
 Grease ResistantDAM
 LubricatedDAM
 Mold Release, GoodDAM
 Moldability, GoodDAM
 Molding Cycle, FastDAM
 Molecular Wt., LowDAM
 Oil ResistantDAM
 Processability, GoodDAM
 Wear Resistance, GoodDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryUnreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 ConnectorsDAM
 Electrical/Electronic ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45438.html

免责声明: 本文 DuPont Performance Polymers Zytel® 101L NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4