- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 2.80
- 热变形温度 [℃]: 195.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 85.0 MPa @Temperature 23.0 °C | 12300 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 15 % @Temperature 23.0 °C | 15 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| Elongation at Yield | 4.3 % @Temperature 23.0 °C | 4.3 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 200 kJ/m² @Temperature 23.0 °C | 95.2 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1U | ||
| Charpy Impact Unnotched | 25.0 J/cm² @Temperature 23.0 °C | 119 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 95.0 °C @Thickness 0.710 mm | 203 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 110 °C @Thickness 1.50 mm | 230 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 110 °C @Thickness 3.00 mm | 230 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 115 °C @Thickness 0.710 mm | 239 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| Flammability, UL94 | V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; IEC 60695-11-10 | ||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; UL94 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; UL94 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; UL94 | |||
| Glow Wire Test | 725 °C @Thickness 0.710 mm | 1340 °F @Thickness 0.0280 in | DAM; Ignition; IEC 60695-2-13 | ||
| 725 °C @Thickness 1.50 mm | 1340 °F @Thickness 0.0591 in | DAM; Ignition; IEC 60695-2-13 | |||
| 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | DAM; Ignition; IEC 60695-2-13 | |||
| 850 °C @Thickness 0.710 mm | 1560 °F @Thickness 0.0280 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | DAM; IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Lubricant | DAM | ||||
| Mold Release | DAM | ||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Cycle (Production), Fast | DAM | ||||
| Electrical Properties, Good | DAM | ||||
| Fatigue Resistant | DAM | ||||
| Flow, High | DAM | ||||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Mold Release, Good | DAM | ||||
| Moldability, Good | DAM | ||||
| Molding Cycle, Fast | DAM | ||||
| Oil Resistant | DAM | ||||
| Processability, Good | DAM | ||||
| Thermal Aging Resistance, Good | DAM | ||||
| Wear Resistance, Good | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Connectors | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Fasteners | DAM | ||||