- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.908
- 拉伸强度 [MPa]: 150.0
- 断裂伸长率 [%]: 175
- 弯曲强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 0.0108
- 硬度: 65.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.80 g/cc | 0.0470 - 0.0650 lb/in³ | Average value: 1.56 g/cc Grade Count:164 |
| Filler Content | 45.0 - 50.0 % | 45.0 - 50.0 % | Average value: 48.2 % Grade Count:30 |
| Water Absorption | 0.200 - 5.10 % | 0.200 - 5.10 % | Average value: 2.22 % Grade Count:92 |
| Moisture Absorption at Equilibrium | 0.250 - 4.80 % | 0.250 - 4.80 % | Average value: 1.35 % Grade Count:58 |
| Water Absorption at Saturation | 0.500 - 8.00 % | 0.500 - 8.00 % | Average value: 4.64 % Grade Count:13 |
| 0.750 - 1.60 % @Treatment Temp. 70.0 - 70.0 °C | 0.750 - 1.60 % @Treatment Temp. 158 - 158 °F | Average value: 1.26 % Grade Count:1 | |
| 0.750 - 1.60 % @Temperature 50.0 - 435 °C | 0.750 - 1.60 % @Temperature 122 - 815 °F | Average value: 1.26 % Grade Count:1 | |
| Viscosity | 100 - 400 cP @Temperature 230 - 270 °C | 100 - 400 cP @Temperature 446 - 518 °F | Average value: 212 cP Grade Count:1 |
| 100 - 400 cP @Shear Rate 100 - 1000 1/s | 100 - 400 cP @Shear Rate 100 - 1000 1/s | Average value: 212 cP Grade Count:1 | |
| Viscosity Measurement | 0.400 - 145 | 0.400 - 145 | Average value: 88.9 Grade Count:11 |
| Viscosity Test | 140 - 150 cm³/g | 140 - 150 cm³/g | Average value: 143 cm³/g Grade Count:3 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:14 |
| Linear Mold Shrinkage | 0.000200 - 0.0350 cm/cm | 0.000200 - 0.0350 in/in | Average value: 0.00326 cm/cm Grade Count:119 |
| 0.00200 - 0.00200 cm/cm @Temperature 80.0 - 80.0 °C | 0.00200 - 0.00200 in/in @Temperature 176 - 176 °F | Average value: 0.00200 cm/cm Grade Count:6 | |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 cm/cm | 0.00300 in/in | Average value: 0.00300 cm/cm Grade Count:3 |
| Linear Mold Shrinkage, Transverse | 0.000500 - 0.0141 cm/cm | 0.000500 - 0.0141 in/in | Average value: 0.00683 cm/cm Grade Count:50 |
| 0.00600 - 0.00600 cm/cm @Temperature 80.0 - 80.0 °C | 0.00600 - 0.00600 in/in @Temperature 176 - 176 °F | Average value: 0.00600 cm/cm Grade Count:6 | |
| Melt Flow | 1.00 - 38.8 g/10 min | 1.00 - 38.8 g/10 min | Average value: 16.8 g/10 min Grade Count:14 |
| Spiral Flow | 430 - 700 cm | 169 - 276 in | Average value: 610 cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 65.0 - 212 | 65.0 - 212 | Average value: 122 Grade Count:32 |
| Hardness, Shore D | 78.0 - 98.0 | 78.0 - 98.0 | Average value: 87.5 Grade Count:10 |
| Ball Indentation Hardness | 140 - 280 MPa | 20300 - 40600 psi | Average value: 205 MPa Grade Count:9 |
| Tensile Strength, Ultimate | 25.0 - 605 MPa | 3630 - 87700 psi | Average value: 190 MPa Grade Count:111 |
| 90.0 - 321.64 MPa @Temperature -40.0 - 121 °C | 13100 - 46650 psi @Temperature -40.0 - 250 °F | Average value: 102 MPa Grade Count:3 | |
| 72.5 - 115 MPa @Time 1.80e+7 - 7.20e+7 sec | 10500 - 16700 psi @Time 5000 - 20000 hour | Average value: 102 MPa Grade Count:2 | |
| 72.5 - 115 MPa @Temperature 130 - 175 °C | 10500 - 16700 psi @Temperature 266 - 347 °F | Average value: 102 MPa Grade Count:2 | |
| 11.61 - 261.67 MPa @Temperature -20.0 - 150 °C | 1684 - 37952 psi @Temperature -4.00 - 302 °F | Average value: 102 MPa Grade Count:1 | |
| 11.61 - 261.67 MPa @Strain 0.220 - 6.70 % | 1684 - 37952 psi @Strain 0.220 - 6.70 % | Average value: 102 MPa Grade Count:1 | |
| Tensile Strength, Yield | 150 - 240 MPa | 21800 - 34800 psi | Average value: 202 MPa Grade Count:48 |
| Elongation at Break | 1.00 - 6.00 % | 1.00 - 6.00 % | Average value: 3.04 % Grade Count:141 |
| 2.30 - 2.60 % @Temperature -40.0 - 121 °C | 2.30 - 2.60 % @Temperature -40.0 - 250 °F | Average value: 2.45 % Grade Count:1 | |
| Elongation at Yield | 1.00 - 4.50 % | 1.00 - 4.50 % | Average value: 2.65 % Grade Count:10 |
| Modulus of Elasticity | 0.0130 - 30.1 GPa | 1.89 - 4370 ksi | Average value: 13.7 GPa Grade Count:99 |
| 4.415 - 15.9958 GPa @Temperature -40.0 - 150 °C | 640.4 - 2320.04 ksi @Temperature -40.0 - 302 °F | Average value: 9.95 GPa Grade Count:2 | |
| Flexural Yield Strength | 175 - 840 MPa | 25400 - 122000 psi | Average value: 309 MPa Grade Count:106 |
| 100 - 433.06 MPa @Temperature -40.0 - 121 °C | 14500 - 62810 psi @Temperature -40.0 - 250 °F | Average value: 243 MPa Grade Count:3 | |
| Flexural Modulus | 0.0108 - 26.5 GPa | 1.56 - 3840 ksi | Average value: 12.3 GPa Grade Count:116 |
| 4.50 - 15.4443 GPa @Temperature -40.0 - 121 °C | 653 - 2240.03 ksi @Temperature -40.0 - 250 °F | Average value: 9.54 GPa Grade Count:4 | |
| Compressive Yield Strength | 160 - 274 MPa | 23200 - 39700 psi | Average value: 208 MPa Grade Count:5 |
| Shear Modulus | 0.392 - 2.488 GPa @Temperature -50.0 - 210 °C | 56.9 - 360.9 ksi @Temperature -58.0 - 410 °F | Average value: 1.33 GPa Grade Count:1 |
| Izod Impact, Notched | 0.908 - 4.97 J/cm | 1.70 - 9.30 ft-lb/in | Average value: 2.08 J/cm Grade Count:61 |
| 1.15 - 5.97968 J/cm @Temperature -40.0 - 121 °C | 2.15 - 11.2024 ft-lb/in @Temperature -40.0 - 250 °F | Average value: 2.25 J/cm Grade Count:3 | |
| 1.01441 - 1.01441 J/cm @Thickness 3.17 - 3.17 mm | 1.90041 - 1.90041 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 2.25 J/cm Grade Count:1 | |
| 1.01441 - 1.01441 J/cm @Temperature -40.0 - -40.0 °C | 1.90041 - 1.90041 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 2.25 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 7.47 - 5340 J/cm | 14.0 - 10000 ft-lb/in | Average value: 12.2 J/cm Grade Count:35 |
| Izod Impact, Notched (ISO) | 12.0 - 147 kJ/m² | 5.71 - 69.8 ft-lb/in² | Average value: 21.2 kJ/m² Grade Count:44 |
| 11.0 - 20.0 kJ/m² @Temperature -40.0 - -20.0 °C | 5.23 - 9.52 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 14.4 kJ/m² Grade Count:13 | |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² - NB | 33.3 ft-lb/in² - NB | Average value: 90.6 kJ/m² Grade Count:13 |
| 75.0 kJ/m² - NB @Temperature -30.0 - -30.0 °C | 35.7 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F | Average value: 88.1 kJ/m² Grade Count:7 | |
| Charpy Impact Unnotched | 1.50 J/cm² - NB | 7.14 ft-lb/in² - NB | Average value: 9.22 J/cm² Grade Count:83 |
| 1.40 - 999.9 J/cm² @Temperature -40.0 - 30.0 °C | 6.66 - 4759 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 8.07 J/cm² Grade Count:52 | |
| Charpy Impact, Notched | 0.600 - 3.90 J/cm² | 2.86 - 18.6 ft-lb/in² | Average value: 1.94 J/cm² Grade Count:78 |
| 0.850 - 2.30 J/cm² @Temperature -40.0 - 30.0 °C | 4.05 - 10.9 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 1.34 J/cm² Grade Count:45 | |
| Puncture Energy | 3.60 - 14.0 J | 2.66 - 10.3 ft-lb | Average value: 7.65 J Grade Count:6 |
| 3.40 - 6.00 J @Temperature -30.0 - -30.0 °C | 2.51 - 4.43 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 4.36 J Grade Count:4 | |
| 3.50 - 3.50 J @Load <=91.8 kg | 2.58 - 2.58 ft-lb @Load <=202 lb | Average value: 4.36 J Grade Count:1 | |
| 3.50 - 3.50 J @Temperature -30.0 - -30.0 °C | 2.58 - 2.58 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 4.36 J Grade Count:1 | |
| Tensile Creep Modulus, 1 hour | 8100 - 9400 MPa | 1.17e+6 - 1.36e+6 psi | Average value: 8750 MPa Grade Count:6 |
| Tensile Creep Modulus, 1000 hours | 6600 - 10500 MPa | 957000 - 1.52e+6 psi | Average value: 7450 MPa Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.00e+16 ohm-cm | 100 - 1.00e+16 ohm-cm | Average value: 7.49e+14 ohm-cm Grade Count:73 |
| Surface Resistance | 100 - 1.00e+16 ohm | 100 - 1.00e+16 ohm | Average value: 9.66e+14 ohm Grade Count:32 |
| Dielectric Constant | 3.00 - 14.0 | 3.00 - 14.0 | Average value: 5.75 Grade Count:36 |
| Dielectric Strength | 15.4 - 80.0 kV/mm | 390 - 2030 kV/in | Average value: 31.0 kV/mm Grade Count:59 |
| Dissipation Factor | 0.00500 - 0.300 | 0.00500 - 0.300 | Average value: 0.0822 Grade Count:30 |
| Arc Resistance | 92.0 - 130 sec | 92.0 - 130 sec | Average value: 112 sec Grade Count:4 |
| Comparative Tracking Index | 350 - 600 V | 350 - 600 V | Average value: 537 V Grade Count:46 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.100 - 500 µm/m-°C | 0.0556 - 278 µin/in-°F | Average value: 39.4 µm/m-°C Grade Count:58 |
| CTE, linear, Transverse to Flow | 0.180 - 120 µm/m-°C | 0.100 - 66.7 µin/in-°F | Average value: 69.6 µm/m-°C Grade Count:27 |
| Specific Heat Capacity | 1.00 - 1.30 J/g-°C | 0.239 - 0.311 BTU/lb-°F | Average value: 1.15 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.320 - 0.380 W/m-K | 2.22 - 2.64 BTU-in/hr-ft²-°F | Average value: 0.350 W/m-K Grade Count:4 |
| Melting Point | 215 - 285 °C | 419 - 545 °F | Average value: 222 °C Grade Count:88 |
| Maximum Service Temperature, Air | 65.0 - 260 °C | 149 - 500 °F | Average value: 150 °C Grade Count:23 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 - 250 °C | 410 - 482 °F | Average value: 219 °C Grade Count:81 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 - 256 °C | 392 - 493 °F | Average value: 214 °C Grade Count:133 |
| Deflection Temperature at 8.0 MPa | 140 - 185 °C | 284 - 365 °F | Average value: 171 °C Grade Count:10 |
| Vicat Softening Point | 200 - 223 °C | 392 - 433 °F | Average value: 208 °C Grade Count:24 |
| Decomposition Temperature | 300 - 350 °C | 572 - 662 °F | Average value: 317 °C Grade Count:3 |
| UL RTI, Electrical | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:11 |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:11 |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:11 |
| Flammability, UL94 | HB | HB | Grade Count:88 |
| Oxygen Index | 23.0 - 25.0 % | 23.0 - 25.0 % | Average value: 24.1 % Grade Count:7 |
| Glow Wire Test | 550 - 675 °C | 1020 - 1250 °F | Average value: 647 °C Grade Count:20 |
| Shrinkage | 0.0200 - 0.0500 % @Time 14400 - 14400 sec | 0.0200 - 0.0500 % @Time 4.00 - 4.00 hour | Average value: 0.0350 % Grade Count:1 |
| 0.0200 - 0.0500 % @Temperature 120 - 120 °C | 0.0200 - 0.0500 % @Temperature 248 - 248 °F | Average value: 0.0350 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 300 °C | 158 - 572 °F | Average value: 203 °C Grade Count:17 |
| Feed Temperature | 20.0 - 270 °C | 68.0 - 518 °F | Average value: 179 °C Grade Count:12 |
| Nozzle Temperature | 230 - 290 °C | 446 - 554 °F | Average value: 263 °C Grade Count:7 |
| Melt Temperature | 80.0 - 330 °C | 176 - 626 °F | Average value: 256 °C Grade Count:65 |
| Mold Temperature | 50.0 - 121 °C | 122 - 250 °F | Average value: 86.8 °C Grade Count:58 |
| Drying Temperature | 70.0 - 110 °C | 158 - 230 °F | Average value: 83.2 °C Grade Count:59 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.88 hour Grade Count:47 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:2 | |
| Moisture Content | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.148 % Grade Count:40 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -23.6 °C Grade Count:4 |
| Injection Pressure | 4.96 - 150 MPa | 720 - 21800 psi | Average value: 81.1 MPa Grade Count:21 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:3 |
| Back Pressure | 0.138 - 1.72 MPa | 20.0 - 250 psi | Average value: 0.752 MPa Grade Count:4 |
| Screw Speed | 20.0 - 200 rpm | 20.0 - 200 rpm | Average value: 81.7 rpm Grade Count:3 |