- 密度 [g/cm3]: 1.38
- 拉伸强度 [MPa]: 115.0
- 断裂伸长率 [%]: 180
- 弯曲强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 5.125
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | 6.0 % | 6.0 % | Nominal strain at break, ISO, 50 mm/min |
| 6.0 % | 6.0 % | Strain at break, ASTM, 5 mm/min | |
| Elongation at Yield | 5.9 % | 5.9 % | ISO Value at 50 mm/min. |
| 6.0 % | 6.0 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 5.84 GPa | 847 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 180 MPa | 26100 psi | ASTM Data |
| Flexural Modulus | 5.125 GPa | 743.3 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |