- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 拉伸强度 [MPa]: 84.0
- 断裂伸长率 [%]: 110
- 弯曲模量 [MPa]: 2.59
- 热变形温度 [℃]: 178.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO data |
| Water Absorption | 1.6 % | 1.6 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 9.5 % | 9.5 % | in water; 23°C; ISO data |
| Viscosity Measurement | 48 | 48 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO value at 50 mm/min. |
| 85.0 MPa | 12300 psi | ASTM value at 50 mm/min. | |
| Elongation at Break | 50 % | 50 % | Nominal strain at break, ISO, 50 mm/min |
| 50 % | 50 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 3.0 % | 3.0 % | ISO Value at 50 mm/min. |
| 4.0 % | 4.0 % | ASTM Value at 50 mm/min. | |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM Data |
| Flexural Modulus | 2.59 GPa | 376 ksi | ISO Value |
| 2.83 GPa | 410 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 83.0 µm/m-°C @Temperature 20.0 °C | 46.1 µin/in-°F @Temperature 68.0 °F | ASTM data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM Data |
| Flammability, UL94 | V-2 @Thickness 0.700 mm | V-2 @Thickness 0.0276 in | |
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |