- 吸水率 [%]: 1.6
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | DIN 53 479 | ||
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | Absorption of humidity in standard operating environment; DIN 53 715 | ||
| Water Absorption at Saturation | 1.6 % | 1.6 % | DIN 53 495 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 95.0 MPa @Time 30.0 sec | 13800 psi @Time 0.00833 hour | DIN 53 456 | ||
| Tensile Strength | 35.0 MPa | 5080 psi | DIN 53 455 | ||
| Elongation at Break | 240 % | 240 % | DIN 53 455 | ||
| Tensile Modulus | 1.80 GPa | 261 ksi | DIN 53 457 | ||
| Charpy Impact, Notched | NB | NB | DIN 53 453 | ||
| Coefficient of Friction, Dynamic | 0.32 - 0.38 | 0.32 - 0.38 | Against steel, p=0.05 N/mm², v=0.6 m/s, hardened and ground | ||
| Tear Strength Test | 46 - 52 | 46 - 52 | in MPa; DIN 53 455 | ||
| Abrasion | 0.80 | 0.80 | µm/km; Against steel, p=0.05 N/mm², v=0.6 m/s, hardened and ground | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | DIN 53 482, VDE 0303, Part 3 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53 482 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | DIN 53 483, IEC-250 | ||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | Breakdown; DIN 53 481, IEC-243, VDE 0303 Part 1 | ||
| Dielectric Loss Index | 0.040 @Frequency 1.00e+6 Hz | 0.040 @Frequency 1.00e+6 Hz | DIN 53 483, IEC-250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | |||
| Specific Heat Capacity | 2.10 J/g-°C | 0.502 BTU/lb-°F | |||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | |||
| Melting Point | 179 °C | 354 °F | DIN 53 736 | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous use | ||
| 150 °C | 302 °F | Short Periods | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO-R 75 Method B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO-R 75 Method A | ||
| Glass Transition Temp, Tg | 41.0 °C | 106 °F | dynamic; DIN 53 736 | ||
| Flammability, UL94 | V-2 | V-2 | |||
| Descriptive Properties | |||||
| Color | natural | ||||
| Creep Resistance | Grade CTI 600 | DIN 53 480, IEC-112, VDE 0303 Part 1 | |||
| Resistance to hot water, suds | resistant | ||||