- 密度 [g/cm3]: 1.21
- 缺口冲击强度: 0.74
- 拉伸强度 [MPa]: 200.0
- 弯曲模量 [MPa]: 12.41
- 热变形温度 [℃]: 213.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Time 86400 sec | 0.0025 in/in @Time 24.0 hour | ISO 294 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec | 0.0020 - 0.0040 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec | 0.010 - 0.012 in/in @Time 24.0 hour | ASTM D955 |
| 0.011 cm/cm @Time 86400 sec | 0.011 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527 |
| 201 MPa | 29200 psi | ASTM D638 | |
| Tensile Strength, Yield | 200 MPa | 29000 psi | ISO 527 |
| 201 MPa | 29200 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 17.92 GPa | 2599 ksi | 50 mm/min; ASTM D638 |
| 18.76 GPa | 2721 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| 284 MPa | 41200 psi | ISO 178 | |
| Flexural Modulus | 12.41 GPa | 1800 ksi | ASTM D790 |
| 15.4 GPa | 2230 ksi | ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.90 J/cm | 14.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 77.4 µm/m-°C @Temperature -40.0 - 40.0 °C | 43.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 78.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 43.3 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 19.8 µm/m-°C @Temperature -40.0 - 40.0 °C | 11.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 20.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 11.1 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 212 °C @Thickness 3.20 mm | 414 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 197 °C @Thickness 3.20 mm | 387 °F @Thickness 0.126 in | unannealed; ASTM D648 | |