- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 4.82
- 热变形温度 [℃]: 203.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D 792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | 50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0066 cm/cm @Time 86400 sec | 0.0066 in/in @Time 24.0 hour | ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec | 0.0060 - 0.0080 in/in @Time 24.0 hour | ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Time 86400 sec | 0.015 in/in @Time 24.0 hour | ISO 294 |
| 0.014 - 0.016 cm/cm @Time 86400 sec | 0.014 - 0.016 in/in @Time 24.0 hour | ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D 638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D 638 |
| Elongation at Break | 22 % | 22 % | ASTM D 638 |
| Tensile Modulus | 6.71 GPa | 973 ksi | 1 mm/min; ISO 527 |
| 10.34 GPa | 1500 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D 790 |
| 138 MPa | 20000 psi | ISO 178 | |
| Flexural Modulus | 4.82 GPa | 699 ksi | ASTM D 790 |
| 5.30 GPa | 769 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C | 0.993 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 3.84 J/cm @Temperature 23.0 °C | 7.19 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 44.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C | 26.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 26.1 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 203 °C @Thickness 3.20 mm | 397 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm | 394 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |