- 密度 [g/cm3]: 1.18
- 缺口冲击强度: 0.37
- 拉伸强度 [MPa]: 47.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.017 - 0.019 cm/cm @Time 86400 sec | 0.017 - 0.019 in/in @Time 24.0 hour | ASTM D955 |
| 0.018 cm/cm @Time 86400 sec | 0.018 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.017 - 0.019 cm/cm @Time 86400 sec | 0.017 - 0.019 in/in @Time 24.0 hour | ASTM D955 |
| 0.018 cm/cm @Time 86400 sec | 0.018 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ASTM D638 |
| 49.0 MPa | 7110 psi | ISO 527 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | ASTM D638 |
| 49.0 MPa | 7110 psi | ISO 527 | |
| Elongation at Break | 14.3 % | 14.3 % | ASTM D638 |
| 15.6 % | 15.6 % | ISO 527 | |
| Elongation at Yield | 13.6 % | 13.6 % | ASTM D638 |
| 15.2 % | 15.2 % | ISO 527 | |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| 2.19 GPa | 318 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| 2.06 GPa | 299 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.71 J/cm | 10.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.27 | 0.27 | ASTM D3702 Modified |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 157 °C @Thickness 3.20 mm | 315 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 61.0 °C @Thickness 3.20 mm | 142 °F @Thickness 0.126 in | unannealed; ASTM D648 | |