- 密度 [g/cm3]: 1.2
- 缺口冲击强度: 0.39
- 拉伸强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 1.71
- 热变形温度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.260 % | 0.260 % | 50% RH, 24 hrs; ASTM D570 |
| 0.370 % | 0.370 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec | >= 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 |
| 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 11.4 % | 11.4 % | 5 mm/min; ISO 527 |
| 15.8 % | 15.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 10.8 % | 10.8 % | 5 mm/min; ISO 527 |
| 14.2 % | 14.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.43 GPa | 352 ksi | 50 mm/min; ASTM D638 |
| 2.48 GPa | 360 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 1.71 GPa | 248 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.32 GPa | 336 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.75 J/cm | 12.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature -30.0 - 30.0 °C | 61.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature -30.0 - 30.0 °C | 61.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 181 °C @Thickness 3.20 mm | 358 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 56.0 °C @Thickness 3.20 mm | 133 °F @Thickness 0.126 in | unannealed; ASTM D648 | |