LCP V143XL 材料说明：LCP／PPS共混。保持最具有改进的熔接强度、平整度在一定的几何形状e130i特点。40%玻璃增强。
LCP V143XL 形式：粒子
LCP V143XL 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0150 % | 0.0150 % | 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 0.0440 % | 0.0440 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.30 % | 1.30 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 16.0 GPa | 2320 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 225 MPa | 32600 psi | ISO 178 |
| Flexural Modulus | 15.7 GPa | 2280 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 3.50 @Frequency 1.00e+6 Hz |
3.50 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.30 @Frequency 2.05e+9 Hz |
4.30 @Frequency 2.05e+9 Hz |
||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0160 @Frequency 1.00e+6 Hz |
0.0160 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 70.0 @Frequency 2.05e+9 Hz |
70.0 @Frequency 2.05e+9 Hz |
||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C | 4.44 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 31.0 µm/m-°C | 17.2 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ISO 75-1, -2 |