LCP 17311 EFT 材料说明：泽尼特«EFT 17311是一个35%的玻璃和矿物增强级。这种等级提供了良好的流动性，低翘曲，优良的表面外观，和优异的尺寸稳定性。本等级的应用是细间距连接器与薄壁。
LCP 17311 EFT 加工方法：注塑成型
LCP 17311 EFT 的物性表：
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.00 % | 2.00 % | 5mm/min; ISO 527-2/1A |
| 2.40 % | 2.40 % | flexural; ISO 178 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.18 @Frequency 2.05e+9 Hz |
4.18 @Frequency 2.05e+9 Hz |
|
| Dissipation Factor | 4.00 @Frequency 2.05e+9 Hz |
4.00 @Frequency 2.05e+9 Hz |
|
| Thermal Properties | Metric | English | Comments |
| Melting Point | 346 °C | 655 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 298 °C | 568 °F | |