- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.374
- 断裂伸长率 [%]: 48.3
- 弯曲强度 [MPa]: 34.5
- 弯曲模量 [MPa]: 2.76
- 硬度: 85.0
- 热变形温度 [℃]: 132.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 - 1.23 g/cc | 0.0376 - 0.0444 lb/in³ | Average value: 1.17 g/cc Grade Count:8 |
| Filler Content | 10.0 - 20.0 % | 10.0 - 20.0 % | Average value: 15.0 % Grade Count:4 |
| Water Absorption | 0.0100 - 0.0200 % | 0.0100 - 0.0200 % | Average value: 0.0120 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00200 - 0.00700 cm/cm | 0.00200 - 0.00700 in/in | Average value: 0.00417 cm/cm Grade Count:6 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00500 - 0.00900 cm/cm | 0.00500 - 0.00900 in/in | Average value: 0.00650 cm/cm Grade Count:4 |
| Melt Flow | 2.50 - 6.00 g/10 min | 2.50 - 6.00 g/10 min | Average value: 3.83 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 85.0 - 120 | 85.0 - 120 | Average value: 96.7 Grade Count:3 |
| Tensile Strength, Ultimate | 34.5 - 72.0 MPa | 5000 - 10400 psi | Average value: 48.5 MPa Grade Count:6 |
| 18.0 - 40.0 MPa @Temperature 60.0 - 120 °C | 2610 - 5800 psi @Temperature 140 - 248 °F | Average value: 29.3 MPa Grade Count:1 | |
| Elongation at Break | 2.50 - 5.00 % | 2.50 - 5.00 % | Average value: 3.43 % Grade Count:7 |
| Modulus of Elasticity | 3.59 - 5.52 GPa | 520 - 800 ksi | Average value: 4.73 GPa Grade Count:6 |
| Flexural Yield Strength | 48.3 - 80.0 MPa | 7000 - 11600 psi | Average value: 64.4 MPa Grade Count:6 |
| Flexural Modulus | 2.76 - 4.80 GPa | 400 - 696 ksi | Average value: 3.83 GPa Grade Count:6 |
| 1.95 - 3.25 GPa @Temperature 60.0 - 120 °C | 283 - 471 ksi @Temperature 140 - 248 °F | Average value: 2.59 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.374 - 0.800 J/cm | 0.700 - 1.50 ft-lb/in | Average value: 0.544 J/cm Grade Count:7 |
| 0.400 - 0.450 J/cm @Temperature -40.0 - -20.0 °C | 0.749 - 0.843 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.425 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 3.20 - 4.81 J/cm | 6.00 - 9.00 ft-lb/in | Average value: 3.74 J/cm Grade Count:4 |
| Charpy Impact Unnotched | 1.70 - 1.70 J/cm² @Temperature -40.0 - -20.0 °C | 8.09 - 8.09 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 1.70 J/cm² Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | Average value: 8.20e+15 ohm-cm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 - 163 °C | 270 - 325 °F | Average value: 145 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 - 145 °C | 265 - 293 °F | Average value: 137 °C Grade Count:8 |
| Flammability, UL94 | HB | HB | Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 240 °C | 380 - 464 °F | Average value: 212 °C Grade Count:5 |
| Mold Temperature | 18.0 - 71.0 °C | 64.4 - 160 °F | Average value: 47.9 °C Grade Count:7 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:4 |