- 熔体流动速率 [g/10min]: 0.6
- 密度 [g/cm3]: 0.92
- 缺口冲击强度: 0.214
- 拉伸强度 [MPa]: 15.0
- 断裂伸长率 [%]: 17.0
- 弯曲强度 [MPa]: 13.0
- 弯曲模量 [MPa]: 0.640
- 硬度: 50.0
- 热变形温度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 - 1.20 g/cc | 0.0332 - 0.0434 lb/in³ | Average value: 0.988 g/cc Grade Count:133 |
| Filler Content | 7.00 - 20.0 % | 7.00 - 20.0 % | Average value: 12.2 % Grade Count:58 |
| Linear Mold Shrinkage | 0.00100 - 0.0264 cm/cm | 0.00100 - 0.0264 in/in | Average value: 0.0124 cm/cm Grade Count:102 |
| 0.00600 - 0.00900 cm/cm @Temperature 80.0 - 121 °C | 0.00600 - 0.00900 in/in @Temperature 176 - 250 °F | Average value: 0.00750 cm/cm Grade Count:1 | |
| 0.00600 - 0.00900 cm/cm @Time 3600 - 3600 sec | 0.00600 - 0.00900 in/in @Time 1.00 - 1.00 hour | Average value: 0.00750 cm/cm Grade Count:1 | |
| Linear Mold Shrinkage, Transverse | 0.00980 - 0.0271 cm/cm | 0.00980 - 0.0271 in/in | Average value: 0.0159 cm/cm Grade Count:14 |
| Melt Flow | 0.600 - 60.0 g/10 min | 0.600 - 60.0 g/10 min | Average value: 14.5 g/10 min Grade Count:116 |
| Ash | 8.00 - 30.0 % | 8.00 - 30.0 % | Average value: 14.2 % Grade Count:23 |
| 13.0 - 13.0 % @Temperature 950 - 950 °C | 13.0 - 13.0 % @Temperature 1740 - 1740 °F | Average value: 13.0 % Grade Count:1 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 53.0 - 101 | 53.0 - 101 | Average value: 69.0 Grade Count:3 |
| Hardness, Rockwell R | 50.0 - 100 | 50.0 - 100 | Average value: 80.3 Grade Count:29 |
| Hardness, Shore D | 54.0 - 82.0 | 54.0 - 82.0 | Average value: 69.9 Grade Count:32 |
| Tensile Strength, Ultimate | 13.0 - 105 MPa | 1890 - 15200 psi | Average value: 27.9 MPa Grade Count:85 |
| Tensile Strength, Yield | 15.0 - 39.0 MPa | 2180 - 5660 psi | Average value: 27.0 MPa Grade Count:63 |
| Elongation at Break | 4.00 - 400 % | 4.00 - 400 % | Average value: 49.0 % Grade Count:58 |
| Elongation at Yield | 3.30 - 50.0 % | 3.30 - 50.0 % | Average value: 10.3 % Grade Count:40 |
| Modulus of Elasticity | 1.00 - 5.10 GPa | 145 - 740 ksi | Average value: 1.79 GPa Grade Count:35 |
| Flexural Yield Strength | 17.0 - 105 MPa | 2470 - 15200 psi | Average value: 37.5 MPa Grade Count:63 |
| Flexural Modulus | 0.640 - 4.70 GPa | 92.8 - 682 ksi | Average value: 1.81 GPa Grade Count:131 |
| 2.50 - 2.50 GPa @Temperature -20.0 - -20.0 °C | 363 - 363 ksi @Temperature -4.00 - -4.00 °F | Average value: 2.50 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.214 - 13.3 J/cm | 0.400 - 25.0 ft-lb/in | Average value: 1.29 J/cm Grade Count:83 |
| Izod Impact, Unnotched | 2.40 - 16.0 J/cm | 4.50 - 30.0 ft-lb/in | Average value: 6.99 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 2.70 - 54.0 kJ/m² | 1.28 - 25.7 ft-lb/in² | Average value: 19.0 kJ/m² Grade Count:11 |
| 2.00 - 2.30 kJ/m² @Temperature -40.0 - -30.0 °C | 0.952 - 1.09 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 2.10 kJ/m² Grade Count:3 | |
| Charpy Impact Unnotched | 4.20 - 1000 J/cm² | 20.0 - 4760 ft-lb/in² | Average value: 6.03 J/cm² Grade Count:26 |
| 2.00 - 999.9 J/cm² @Temperature -20.0 - -20.0 °C | 9.52 - 4759 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 3.70 J/cm² Grade Count:23 | |
| Charpy Impact, Notched | 0.300 - 7.50 J/cm² | 1.43 - 35.7 ft-lb/in² | Average value: 2.07 J/cm² Grade Count:38 |
| 0.200 - 4.80 J/cm² @Temperature -30.0 - -20.0 °C | 0.952 - 22.8 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.714 J/cm² Grade Count:32 | |
| Gardner Impact | 0.565 - 33.9 J | 0.417 - 25.0 ft-lb | Average value: 5.32 J Grade Count:33 |
| 6.44015 - 6.44015 J @Temperature -30.0 - -30.0 °C | 4.75001 - 4.75001 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 6.44 J Grade Count:1 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 - 110 µm/m-°C | 27.8 - 61.1 µin/in-°F | Average value: 68.6 µm/m-°C Grade Count:11 |
| Melting Point | 135 - 165 °C | 275 - 329 °F | Average value: 157 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 127 °C | 140 - 261 °F | Average value: 109 °C Grade Count:105 |
| Deflection Temperature at 1.8 MPa (264 psi) | 36.0 - 120 °C | 96.8 - 248 °F | Average value: 63.0 °C Grade Count:86 |
| Vicat Softening Point | 50.0 - 155 °C | 122 - 311 °F | Average value: 108 °C Grade Count:35 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:23 |
| Flammability Test | 1.00 - 125 | 1.00 - 125 | Average value: 42.3 Grade Count:3 |
| Glow Wire Test | 650 - 750 °C | 1200 - 1380 °F | Average value: 670 °C Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 200 - 227 °C | 392 - 440 °F | Average value: 215 °C Grade Count:27 |
| Melt Temperature | 170 - 279 °C | 338 - 534 °F | Average value: 216 °C Grade Count:60 |
| Mold Temperature | 10.0 - 80.0 °C | 50.0 - 176 °F | Average value: 45.6 °C Grade Count:60 |
| Drying Temperature | 65.6 - 100 °C | 150 - 212 °F | Average value: 76.3 °C Grade Count:49 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.40 hour Grade Count:47 |
| 2.00 - 4.00 hour @Temperature 71.1 - 71.1 °C | 2.00 - 4.00 hour @Temperature 160 - 160 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.0400 - 0.100 % | 0.0400 - 0.100 % | Average value: 0.0541 % Grade Count:29 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 51.6 MPa Grade Count:53 |
| Hold Pressure | 2.07 - 51.7 MPa | 300 - 7500 psi | Average value: 10.9 MPa Grade Count:24 |
| Back Pressure | 0.000 - 2.00 MPa | 0.000 - 290 psi | Average value: 0.851 MPa Grade Count:35 |