- 熔体流动速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.947
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.502
- 拉伸强度 [MPa]: 20.7
- 断裂伸长率 [%]: 20.7
- 弯曲强度 [MPa]: 16.5
- 弯曲模量 [MPa]: 0.965
- 热变形温度 [℃]: 74.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 - 1.10 g/cc | 0.0342 - 0.0397 lb/in³ | Average value: 1.00 g/cc Grade Count:18 |
| Water Absorption | 0.0100 - 0.0300 % | 0.0100 - 0.0300 % | Average value: 0.0167 % Grade Count:3 |
| Thickness | 102 microns | 4.00 mil | Average value: 102 microns Grade Count:8 |
| Linear Mold Shrinkage | 0.0100 - 0.0200 cm/cm | 0.0100 - 0.0200 in/in | Average value: 0.0146 cm/cm Grade Count:13 |
| Melt Flow | 0.400 - 35.0 g/10 min | 0.400 - 35.0 g/10 min | Average value: 8.14 g/10 min Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 96.0 - 99.0 | 96.0 - 99.0 | Average value: 97.5 Grade Count:8 |
| Hardness, Shore D | 70.0 - 74.0 | 70.0 - 74.0 | Average value: 72.3 Grade Count:8 |
| Tensile Strength, Ultimate | 16.5 - 32.0 MPa | 2390 - 4640 psi | Average value: 23.4 MPa Grade Count:11 |
| Tensile Strength, Yield | 20.7 - 44.8 MPa | 3000 - 6500 psi | Average value: 26.8 MPa Grade Count:7 |
| Film Elongation at Break, MD | 4.00 - 500 % | 4.00 - 500 % | Average value: 252 % Grade Count:4 |
| Elongation at Break | 2.00 - 130 % | 2.00 - 130 % | Average value: 23.0 % Grade Count:13 |
| Elongation at Yield | 7.00 - 12.0 % | 7.00 - 12.0 % | Average value: 9.28 % Grade Count:5 |
| Modulus of Elasticity | 0.483 - 2.20 GPa | 70.1 - 319 ksi | Average value: 1.31 GPa Grade Count:3 |
| Flexural Yield Strength | 20.7 - 48.0 MPa | 3000 - 6960 psi | Average value: 30.0 MPa Grade Count:7 |
| Flexural Modulus | 0.965 - 3.10 GPa | 140 - 450 ksi | Average value: 1.67 GPa Grade Count:17 |
| Izod Impact, Notched | 0.502 - 8.33 J/cm | 0.940 - 15.6 ft-lb/in | Average value: 3.63 J/cm Grade Count:7 |
| Izod Impact, Unnotched | 1.00 J/cm - NB | 1.87 ft-lb/in - NB | Average value: 7.43 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 1.50 kJ/m² - NB | 0.714 ft-lb/in² - NB | Average value: 27.7 kJ/m² Grade Count:10 |
| 1.20 kJ/m² - NB @Temperature -20.0 - -20.0 °C | 0.571 ft-lb/in² - NB @Temperature -4.00 - -4.00 °F | Average value: 5.84 kJ/m² Grade Count:7 | |
| 1.20 kJ/m² - NB @Thickness 4.00 - 4.00 mm | 0.571 ft-lb/in² - NB @Thickness 0.157 - 0.157 in | Average value: 5.84 kJ/m² Grade Count:7 | |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m² - NB | 7.61 ft-lb/in² - NB | Average value: 48.7 kJ/m² Grade Count:10 |
| 9.00 kJ/m² - NB @Temperature -20.0 - -20.0 °C | 4.28 ft-lb/in² - NB @Temperature -4.00 - -4.00 °F | Average value: 17.7 kJ/m² Grade Count:7 | |
| 9.00 kJ/m² - NB @Thickness 4.00 - 4.00 mm | 4.28 ft-lb/in² - NB @Thickness 0.157 - 0.157 in | Average value: 17.7 kJ/m² Grade Count:7 | |
| Charpy Impact Unnotched | 1.40 - 1000 J/cm² | 6.66 - 4760 ft-lb/in² | Average value: 1.40 J/cm² Grade Count:8 |
| 0.500 - 999.9 J/cm² @Temperature -20.0 - -20.0 °C | 2.38 - 4759 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 0.500 J/cm² Grade Count:7 | |
| 0.500 - 999.9 J/cm² @Thickness 102 - 102 mm | 2.38 - 4759 ft-lb/in² @Thickness 4.00 - 4.00 in | Average value: 0.500 J/cm² Grade Count:7 | |
| Charpy Impact, Notched | 0.300 - 5.00 J/cm² | 1.43 - 23.8 ft-lb/in² | Average value: 2.44 J/cm² Grade Count:8 |
| 0.200 - 2.60 J/cm² @Temperature -20.0 - -20.0 °C | 0.952 - 12.4 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 1.39 J/cm² Grade Count:7 | |
| 0.200 - 2.60 J/cm² @Thickness 102 - 102 mm | 0.952 - 12.4 ft-lb/in² @Thickness 4.00 - 4.00 in | Average value: 1.39 J/cm² Grade Count:7 | |
| Film Tensile Strength at Break, MD | 25.0 - 33.0 MPa | 3630 - 4790 psi | Average value: 28.3 MPa Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00 - 1.00e+9 ohm-cm | 5.00 - 1.00e+9 ohm-cm | Average value: 1.00e+8 ohm-cm Grade Count:15 |
| Surface Resistance | 10.0 - 1.00e+9 ohm | 10.0 - 1.00e+9 ohm | Average value: 8.87e+7 ohm Grade Count:17 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 107 - 300 °C | 225 - 572 °F | Average value: 185 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 - 149 °C | 165 - 300 °F | Average value: 99.8 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 - 71.0 °C | 115 - 160 °F | Average value: 55.8 °C Grade Count:13 |
| Vicat Softening Point | 80.0 - 156 °C | 176 - 313 °F | Average value: 134 °C Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 200 - 270 °C | 392 - 518 °F | Average value: 229 °C Grade Count:11 |
| Mold Temperature | 32.2 - 80.0 °C | 90.0 - 176 °F | Average value: 58.9 °C Grade Count:7 |
| Roll Temperature | 60.0 - 100 °C | 140 - 212 °F | Average value: 80.7 °C Grade Count:5 |
| Drying Temperature | 60.0 - 82.2 °C | 140 - 180 °F | Average value: 72.4 °C Grade Count:10 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.20 hour Grade Count:10 |
| Injection Pressure | 60.0 - 80.0 MPa | 8700 - 11600 psi | Average value: 70.0 MPa Grade Count:4 |
| Shelf Life | 12.0 Month | 12.0 Month | Average value: 12.0 Month Grade Count:9 |