- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 0.872
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.427
- 断裂伸长率 [%]: 31.0
- 弯曲强度 [MPa]: 19.3
- 弯曲模量 [MPa]: 2.76
- 热变形温度 [℃]: 132.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.872 - 1.11 g/cc | 0.0315 - 0.0401 lb/in³ | Average value: 0.988 g/cc Grade Count:14 |
| Filler Content | 1.00 - 40.0 % | 1.00 - 40.0 % | Average value: 14.2 % Grade Count:11 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:7 |
| Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00308 cm/cm Grade Count:12 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00150 - 0.00700 cm/cm | 0.00150 - 0.00700 in/in | Average value: 0.00363 cm/cm Grade Count:4 |
| Melt Flow | 1.10 - 9.80 g/10 min | 1.10 - 9.80 g/10 min | Average value: 4.93 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 19.3 - 48.3 MPa | 2800 - 7000 psi | Average value: 34.2 MPa Grade Count:16 |
| Elongation at Break | 0.400 - 436 % | 0.400 - 436 % | Average value: 44.3 % Grade Count:17 |
| Modulus of Elasticity | 1.03 - 18.6 GPa | 150 - 2700 ksi | Average value: 5.85 GPa Grade Count:16 |
| Flexural Yield Strength | 31.0 - 75.8 MPa | 4500 - 11000 psi | Average value: 52.6 MPa Grade Count:13 |
| Flexural Modulus | 2.76 - 13.8 GPa | 400 - 2000 ksi | Average value: 5.91 GPa Grade Count:13 |
| Izod Impact, Notched | 0.427 - 3.20 J/cm | 0.800 - 6.00 ft-lb/in | Average value: 1.03 J/cm Grade Count:13 |
| Izod Impact, Unnotched | 1.07 - 11.2 J/cm | 2.00 - 21.0 ft-lb/in | Average value: 3.59 J/cm Grade Count:13 |
| Charpy Impact, Notched | 0.240 - 0.320 J/cm² | 1.14 - 1.52 ft-lb/in² | Average value: 0.290 J/cm² Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 3.10e+9 ohm-cm | 1.00 - 3.10e+9 ohm-cm | Average value: 2.40e+8 ohm-cm Grade Count:15 |
| Surface Resistance | 100 - 1.10e+11 ohm | 100 - 1.10e+11 ohm | Average value: 1.43e+10 ohm Grade Count:11 |
| Static Decay | 0.100 - 2.00 sec | 0.100 - 2.00 sec | Average value: 1.68 sec Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 °C | 329 °F | Average value: 165 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 - 166 °C | 270 - 330 °F | Average value: 143 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 - 149 °C | 220 - 300 °F | Average value: 127 °C Grade Count:7 |
| Flammability, UL94 | HB | HB | Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 188 - 227 °C | 370 - 440 °F | Average value: 209 °C Grade Count:8 |
| Melt Temperature | 191 - 232 °C | 375 - 450 °F | Average value: 211 °C Grade Count:4 |
| Mold Temperature | 32.2 - 65.6 °C | 90.0 - 150 °F | Average value: 48.5 °C Grade Count:12 |
| Drying Temperature | 79.4 °C | 175 °F | Average value: 79.4 °C Grade Count:4 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:12 |