- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.886
- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 3.38
- 弯曲强度 [MPa]: 19.7
- 弯曲模量 [MPa]: 0.550
- 硬度: 65.0
- 热变形温度 [℃]: 50.0
- 透光率 [%]: 0.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 1.46 g/cc | 0.0320 - 0.0527 lb/in³ | Average value: 0.906 g/cc Grade Count:142 |
| Moisture Vapor Transmission | 4.70 - 14.0 cc-mm/m²-24hr-atm | 11.9 - 35.6 cc-mil/100 in²-24hr-atm | Average value: 8.45 cc-mm/m²-24hr-atm Grade Count:23 |
| Water Vapor Transmission | 0.190 - 10.9 g/m²/day | 0.0122 - 0.702 g/100 in²/day | Average value: 4.80 g/m²/day Grade Count:71 |
| 3.104 - 18.624 g/m²/day @Temperature 37.8 - 37.8 °C | 0.1999 - 1.1994 g/100 in²/day @Temperature 100 - 100 °F | Average value: 10.7 g/m²/day Grade Count:7 | |
| Oxygen Transmission Rate | 0.100 - 2100 cc/m²/day | 0.00644 - 135 cc/100 in²/day | Average value: 139 cc/m²/day Grade Count:19 |
| Thickness | 12.0 - 96.5 microns | 0.472 - 3.80 mil | Average value: 30.7 microns Grade Count:222 |
| Linear Mold Shrinkage | 0.0100 - 0.0400 cm/cm | 0.0100 - 0.0400 in/in | Average value: 0.0346 cm/cm Grade Count:102 |
| Linear Mold Shrinkage, Transverse | 0.0100 - 0.0180 cm/cm | 0.0100 - 0.0180 in/in | Average value: 0.0139 cm/cm Grade Count:101 |
| Melt Flow | 0.350 - 50.0 g/10 min | 0.350 - 50.0 g/10 min | Average value: 5.75 g/10 min Grade Count:183 |
| Antiblock Level | 1800 ppm | 1800 ppm | Average value: 1800 ppm Grade Count:3 |
| Slip Level | 1800 ppm | 1800 ppm | Average value: 1800 ppm Grade Count:3 |
| Coating Weight | 11.4 - 64.6 g/m² | 7.10 - 40.4 lb/ream | Average value: 26.4 g/m² Grade Count:109 |
| Ash | 0.00100 - 0.00200 % | 0.00100 - 0.00200 % | Average value: 0.00150 % Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 65.0 - 113 | 65.0 - 113 | Average value: 93.7 Grade Count:73 |
| Hardness, Shore D | 65.0 - 71.0 | 65.0 - 71.0 | Average value: 68.5 Grade Count:4 |
| Tensile Strength, Ultimate | 19.7 - 152 MPa | 2860 - 22000 psi | Average value: 44.1 MPa Grade Count:16 |
| Film Tensile Strength at Yield, MD | 3.00 - 40.0 MPa | 435 - 5800 psi | Average value: 19.3 MPa Grade Count:21 |
| Film Tensile Strength at Yield, TD | 5.90 - 38.0 MPa | 856 - 5510 psi | Average value: 18.5 MPa Grade Count:21 |
| Tensile Strength, Yield | 3.38 - 48.0 MPa | 490 - 6960 psi | Average value: 32.9 MPa Grade Count:123 |
| Film Elongation at Break, MD | 80.0 - 850 % | 80.0 - 850 % | Average value: 229 % Grade Count:179 |
| Film Elongation at Break, TD | 6.00 - 850 % | 6.00 - 850 % | Average value: 109 % Grade Count:165 |
| Film Elongation at Yield, MD | 12.0 - 15.0 % | 12.0 - 15.0 % | Average value: 13.0 % Grade Count:5 |
| Film Elongation at Yield, TD | 10.0 - 12.0 % | 10.0 - 12.0 % | Average value: 11.2 % Grade Count:5 |
| Elongation at Break | 8.00 - 600 % | 8.00 - 600 % | Average value: 440 % Grade Count:18 |
| Elongation at Yield | 7.00 - 800 % | 7.00 - 800 % | Average value: 19.4 % Grade Count:99 |
| Modulus of Elasticity | 1.05 - 2.05 GPa | 152 - 297 ksi | Average value: 1.44 GPa Grade Count:11 |
| Flexural Modulus | 0.550 - 2.28 GPa | 79.8 - 331 ksi | Average value: 1.38 GPa Grade Count:132 |
| Secant Modulus | 0.480 - 0.793 GPa | 69.6 - 115 ksi | Average value: 0.625 GPa Grade Count:17 |
| Secant Modulus, MD | 0.360 - 2.90 GPa | 52.2 - 420 ksi | Average value: 1.48 GPa Grade Count:30 |
| Secant Modulus, TD | 0.380 - 4.83 GPa | 55.1 - 700 ksi | Average value: 2.29 GPa Grade Count:30 |
| Izod Impact, Notched | 0.200 - 5340 J/cm | 0.375 - 10000 ft-lb/in | Average value: 0.441 J/cm Grade Count:98 |
| 0.170 - 0.267 J/cm @Temperature -20.0 - 0.000 °C | 0.318 - 0.500 ft-lb/in @Temperature -4.00 - 32.0 °F | Average value: 0.208 J/cm Grade Count:4 | |
| Izod Impact, Unnotched | 0.490 J/cm - NB | 0.919 ft-lb/in - NB | Average value: 0.696 J/cm Grade Count:12 |
| 0.294199 - 0.294199 J/cm @Temperature -10.0 - -10.0 °C | 0.551156 - 0.551156 ft-lb/in @Temperature 14.0 - 14.0 °F | Average value: 0.294 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 4.00 - 6.50 kJ/m² | 1.90 - 3.09 ft-lb/in² | Average value: 5.15 kJ/m² Grade Count:13 |
| Charpy Impact, Notched | 0.500 - 55.0 J/cm² | 2.38 - 262 ft-lb/in² | Average value: 6.07 J/cm² Grade Count:10 |
| 0.350 - 12.0 J/cm² @Temperature -23.0 - 0.000 °C | 1.67 - 57.1 ft-lb/in² @Temperature -9.40 - 32.0 °F | Average value: 5.20 J/cm² Grade Count:3 | |
| Gardner Impact | 1.40 - 36.2 J | 1.03 - 26.7 ft-lb | Average value: 20.6 J Grade Count:6 |
| 28.4722 - 28.4722 J @Temperature -30.0 - -29.0 °C | 21.0000 - 21.0000 ft-lb @Temperature -22.0 - -20.2 °F | Average value: 32.3 J Grade Count:2 | |
| Coefficient of Friction | 0.170 - 0.900 | 0.170 - 0.900 | Average value: 0.347 Grade Count:183 |
| Elmendorf Tear Strength MD | 12.0 - 64.0 g | 12.0 - 64.0 g | Average value: 43.7 g Grade Count:3 |
| Elmendorf Tear Strength TD | 88.0 - 300 g | 88.0 - 300 g | Average value: 176 g Grade Count:3 |
| Elmendorf Tear Strength, MD | 0.600 - 1.80 g/micron | 15.2 - 45.7 g/mil | Average value: 1.40 g/micron Grade Count:5 |
| Elmendorf Tear Strength, TD | 2.00 - 9.00 g/micron | 50.8 - 229 g/mil | Average value: 4.10 g/micron Grade Count:5 |
| Dart Drop | 0.780 - 9.40 g/micron | 19.8 - 239 g/mil | Average value: 2.99 g/micron Grade Count:16 |
| Dart drop Test | 20.0 - 350 g | 0.0441 - 0.772 lb | Average value: 200 g Grade Count:8 |
| Seal Strength | 200 g/25 mm | 200 g/in | Average value: 200 g/25 mm Grade Count:8 |
| Film Tensile Strength at Break, MD | 15.0 - 193 MPa | 2180 - 28000 psi | Average value: 121 MPa Grade Count:248 |
| Film Tensile Strength at Break, TD | 8.00 - 305 MPa | 1160 - 44200 psi | Average value: 235 MPa Grade Count:237 |
| Tangent Modulus | 869 - 1620 MPa | 126000 - 235000 psi | Average value: 1120 MPa Grade Count:3 |
| Heat Seal Strength | 518 g/25 mm | 1.14 lb/in | Average value: 518 g/25 mm Grade Count:48 |
| Heat Seal Strength Initiation Temperature | 98.0 - 130 °C | 208 - 266 °F | Average value: 113 °C Grade Count:61 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.25 | 2.25 | Average value: 2.25 Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 119 - 170 °C | 246 - 338 °F | Average value: 154 °C Grade Count:73 |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 - 129 °C | 122 - 264 °F | Average value: 94.5 °C Grade Count:101 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 104 °C | 122 - 219 °F | Average value: 61.9 °C Grade Count:25 |
| Vicat Softening Point | 67.0 - 159 °C | 153 - 318 °F | Average value: 140 °C Grade Count:71 |
| Heat Distortion Temperature | 82.0 - 115 °C | 180 - 239 °F | Average value: 101 °C Grade Count:3 |
| Shrinkage | -4.50 - 26.0 % | -4.50 - 26.0 % | Average value: 4.71 % Grade Count:108 |
| Optical Properties | Metric | English | Comments |
| Optical Density | 2.00 - 2.40 | 2.00 - 2.40 | Average value: 2.24 Grade Count:7 |
| Haze | 0.100 - 90.0 % | 0.100 - 90.0 % | Average value: 6.79 % Grade Count:241 |
| Gloss | 3.00 - 145 % | 3.00 - 145 % | Average value: 83.6 % Grade Count:240 |
| Transmission, Visible | 0.400 - 90.0 % | 0.400 - 90.0 % | Average value: 76.1 % Grade Count:146 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 135 - 255 °C | 275 - 491 °F | Average value: 225 °C Grade Count:7 |
| Melt Temperature | 182 - 274 °C | 360 - 525 °F | Average value: 245 °C Grade Count:34 |