- 密度 [g/cm3]: 0.96
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 19.0
- 断裂伸长率 [%]: 27.6
- 弯曲强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 1.10
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 - 1.30 g/cc | 0.0347 - 0.0470 lb/in³ | Average value: 1.06 g/cc Grade Count:12 |
| Filler Content | 5.00 - 15.0 % | 5.00 - 15.0 % | Average value: 10.0 % Grade Count:4 |
| Water Absorption | 0.0100 - 0.0200 % | 0.0100 - 0.0200 % | Average value: 0.0125 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00300 - 0.0250 cm/cm | 0.00300 - 0.0250 in/in | Average value: 0.00838 cm/cm Grade Count:10 |
| Linear Mold Shrinkage, Transverse | 0.0140 - 0.0250 cm/cm | 0.0140 - 0.0250 in/in | Average value: 0.0223 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 15.0 - 66.0 MPa | 2180 - 9570 psi | Average value: 30.3 MPa Grade Count:12 |
| Tensile Strength, Yield | 19.0 - 21.4 MPa | 2760 - 3100 psi | Average value: 20.5 MPa Grade Count:3 |
| Elongation at Break | 2.50 - 76.0 % | 2.50 - 76.0 % | Average value: 23.8 % Grade Count:12 |
| Elongation at Yield | 5.20 - 7.10 % | 5.20 - 7.10 % | Average value: 6.13 % Grade Count:3 |
| Modulus of Elasticity | 0.965 - 4.10 GPa | 140 - 595 ksi | Average value: 2.05 GPa Grade Count:11 |
| Flexural Yield Strength | 27.6 - 109 MPa | 4000 - 15800 psi | Average value: 48.5 MPa Grade Count:12 |
| Flexural Modulus | 1.10 - 6.20 GPa | 160 - 899 ksi | Average value: 2.50 GPa Grade Count:12 |
| Izod Impact, Notched | 0.600 - 2.67 J/cm | 1.12 - 5.00 ft-lb/in | Average value: 1.60 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 3.20 - 5340 J/cm | 5.99 - 10000 ft-lb/in | Average value: 8.36 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 10.0 - 25.0 kJ/m² | 4.76 - 11.9 ft-lb/in² | Average value: 20.0 kJ/m² Grade Count:3 |
| K (wear) Factor | 10100 x 10-8 mm³/N-M | 5000 x 10-10 in³-min/ft-lb-hr | Average value: 10100 x 10-8 mm³/N-M Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0100 - 100 ohm-cm | 0.0100 - 100 ohm-cm | Average value: 22.6 ohm-cm Grade Count:9 |
| Surface Resistance | 10.0 - 1.00e+6 ohm | 10.0 - 1.00e+6 ohm | Average value: 161000 ohm Grade Count:8 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 - 140 µm/m-°C | 30.0 - 77.8 µin/in-°F | Average value: 103 µm/m-°C Grade Count:4 |
| CTE, linear, Transverse to Flow | 120 - 170 µm/m-°C | 66.7 - 94.4 µin/in-°F | Average value: 150 µm/m-°C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 - 138 °C | 203 - 280 °F | Average value: 127 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 - 138 °C | 127 - 280 °F | Average value: 90.1 °C Grade Count:8 |
| Flammability, UL94 | HB | HB | Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 188 - 227 °C | 370 - 440 °F | Average value: 204 °C Grade Count:3 |
| Melt Temperature | 193 - 246 °C | 380 - 475 °F | Average value: 223 °C Grade Count:6 |
| Mold Temperature | 32.2 - 65.6 °C | 90.0 - 150 °F | Average value: 44.4 °C Grade Count:9 |
| Drying Temperature | 79.4 - 82.2 °C | 175 - 180 °F | Average value: 80.8 °C Grade Count:6 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.50 hour Grade Count:4 |
| Moisture Content | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:3 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:6 |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | Average value: 0.259 MPa Grade Count:3 |