塑胶原料之家
  1. 首页
  2. 英文物性
  3. PP
  4. Overview of materials for Polypropylene with 20% Talc Filler

Overview of materials for Polypropylene with 20% Talc Filler

Overview of materials for Polypropylene with 20% Talc Filler 物性表: Overview of materials for Polypropylene with 20% Talc Filler物性表及特性介绍,Overview of materials for Polypropylene with 20% Talc Filler注塑参数详情,如需Overview of materials for Polypropylene with 20% Talc Filler下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.6
  • 密度 [g/cm3]: 0.97
  • 吸水率 [%]: 0.02
  • 缺口冲击强度: 0.198
  • 拉伸强度 [MPa]: 13.8
  • 断裂伸长率 [%]: 17.0
  • 弯曲强度 [MPa]: 12.0
  • 弯曲模量 [MPa]: 1.02
  • 硬度: 52.0
  • 热变形温度 [℃]: 70.0
 
Physical PropertiesMetricEnglishComments
Density 0.970 - 1.46 g/cc0.0350 - 0.0527 lb/in³Average value: 1.05 g/cc Grade Count:301
Filler Content 10.0 - 30.0 %10.0 - 30.0 %Average value: 19.5 % Grade Count:159
Water Absorption 0.0200 - 0.0300 %0.0200 - 0.0300 %Average value: 0.0267 % Grade Count:15
Linear Mold Shrinkage 0.000900 - 0.0265 cm/cm0.000900 - 0.0265 in/inAverage value: 0.0119 cm/cm Grade Count:239
Linear Mold Shrinkage, 6.35 mm section 0.0150 - 0.0200 cm/cm0.0150 - 0.0200 in/inAverage value: 0.0189 cm/cm Grade Count:8
Linear Mold Shrinkage, Transverse 0.00720 - 0.0272 cm/cm0.00720 - 0.0272 in/inAverage value: 0.0153 cm/cm Grade Count:31
Melt Flow 0.600 - 30.0 g/10 min0.600 - 30.0 g/10 minAverage value: 12.4 g/10 min Grade Count:273
Ash 17.0 - 25.0 %17.0 - 25.0 %Average value: 20.4 % Grade Count:19
 15.0 - 20.0 %
@Temperature 600 - 600 °C		15.0 - 20.0 %
@Temperature 1110 - 1110 °F		Average value: 19.0 % Grade Count:5
Storage Temperature 60.0 °C140 °FAverage value: 60.0 °C Grade Count:5
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 48.0 - 10048.0 - 100Average value: 67.8 Grade Count:4
Hardness, Rockwell R 52.0 - 98.052.0 - 98.0Average value: 86.8 Grade Count:38
Hardness, Shore D 56.0 - 80.056.0 - 80.0Average value: 69.5 Grade Count:66
Tensile Strength, Ultimate 12.0 - 37.0 MPa1740 - 5370 psiAverage value: 26.6 MPa Grade Count:213
Tensile Strength, Yield 13.8 - 39.0 MPa2000 - 5660 psiAverage value: 28.4 MPa Grade Count:104
Elongation at Break 3.00 - 400 %3.00 - 400 %Average value: 31.4 % Grade Count:122
Elongation at Yield 3.00 - 32.0 %3.00 - 32.0 %Average value: 8.64 % Grade Count:129
Modulus of Elasticity 1.10 - 3.45 GPa160 - 500 ksiAverage value: 2.19 GPa Grade Count:85
Flexural Yield Strength 17.0 - 70.0 MPa2470 - 10200 psiAverage value: 42.7 MPa Grade Count:163
Flexural Modulus 1.02 - 4.10 GPa148 - 595 ksiAverage value: 2.07 GPa Grade Count:301
 2.30 - 2.50 GPa
@Temperature -20.0 - -20.0 °C		334 - 363 ksi
@Temperature -4.00 - -4.00 °F		Average value: 2.35 GPa Grade Count:6
Izod Impact, Notched 0.198 - 8.01 J/cm0.370 - 15.0 ft-lb/inAverage value: 0.693 J/cm Grade Count:156
 0.200 - 0.26695 J/cm
@Temperature -40.0 - -20.0 °C		0.375 - 0.50011 ft-lb/in
@Temperature -40.0 - -4.00 °F		Average value: 0.229 J/cm Grade Count:3
Izod Impact, Unnotched 0.350 - 5340 J/cm0.656 - 10000 ft-lb/inAverage value: 6.07 J/cm Grade Count:42
 0.250 - 0.250 J/cm
@Temperature 0.000 - 0.000 °C		0.468 - 0.468 ft-lb/in
@Temperature 32.0 - 32.0 °F		Average value: 0.250 J/cm Grade Count:2
Izod Impact, Notched (ISO) 2.40 - 28.0 kJ/m²1.14 - 13.3 ft-lb/in²Average value: 8.43 kJ/m² Grade Count:14
 1.80 - 4.00 kJ/m²
@Temperature -40.0 - -20.0 °C		0.857 - 1.90 ft-lb/in²
@Temperature -40.0 - -4.00 °F		Average value: 2.41 kJ/m² Grade Count:7
Izod Impact, Unnotched (ISO) 15.0 - 55.0 kJ/m²7.14 - 26.2 ft-lb/in²Average value: 31.3 kJ/m² Grade Count:4
 17.0 - 24.0 kJ/m²
@Temperature -30.0 - -30.0 °C		8.09 - 11.4 ft-lb/in²
@Temperature -22.0 - -22.0 °F		Average value: 20.5 kJ/m² Grade Count:2
Charpy Impact Unnotched 1.50 J/cm² - NB7.14 ft-lb/in² - NBAverage value: 4.92 J/cm² Grade Count:70
 1.00 J/cm² - NB
@Temperature -30.0 - 0.000 °C		4.76 ft-lb/in² - NB
@Temperature -22.0 - 32.0 °F		Average value: 2.56 J/cm² Grade Count:65
Charpy Impact, Notched 0.200 - 7.50 J/cm²0.952 - 35.7 ft-lb/in²Average value: 1.07 J/cm² Grade Count:132
 0.100 - 4.80 J/cm²
@Temperature -40.0 - 0.000 °C		0.476 - 22.8 ft-lb/in²
@Temperature -40.0 - 32.0 °F		Average value: 0.394 J/cm² Grade Count:112
Gardner Impact 0.451 - 271 J0.333 - 200 ft-lbAverage value: 13.4 J Grade Count:74
 1.35582 - 43.3862 J
@Temperature -30.0 - -5.56 °C		1.00000 - 32.0000 ft-lb
@Temperature -22.0 - 22.0 °F		Average value: 13.7 J Grade Count:4
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmAverage value: 1.00e+16 ohm-cm Grade Count:9
Dielectric Strength 19.7 - 24.0 kV/mm500 - 610 kV/inAverage value: 21.1 kV/mm Grade Count:3
Comparative Tracking Index 600 V600 VAverage value: 600 V Grade Count:5
 
Thermal PropertiesMetricEnglishComments
CTE, linear 50.0 - 110 µm/m-°C27.8 - 61.1 µin/in-°FAverage value: 69.1 µm/m-°C Grade Count:25
Melting Point 135 - 182 °C275 - 360 °FAverage value: 157 °C Grade Count:26
Deflection Temperature at 0.46 MPa (66 psi) 70.0 - 144 °C158 - 291 °FAverage value: 114 °C Grade Count:237
Deflection Temperature at 1.8 MPa (264 psi) 25.0 - 133 °C77.0 - 271 °FAverage value: 70.5 °C Grade Count:240
Vicat Softening Point 53.0 - 160 °C127 - 320 °FAverage value: 113 °C Grade Count:120
Flammability, UL94 HB - 5VAHB - 5VAGrade Count:108
Flammability Test 0.600 - 1250.600 - 125Average value: 16.4 Grade Count:8
Oxygen Index 21.0 %21.0 %Average value: 21.0 % Grade Count:4
Glow Wire Test 650 - 960 °C1200 - 1760 °FAverage value: 742 °C Grade Count:59
 
Optical PropertiesMetricEnglishComments
Gloss 45.0 - 47.0 %45.0 - 47.0 %Average value: 46.0 % Grade Count:4
 
Processing PropertiesMetricEnglishComments
Processing Temperature 193 - 227 °C380 - 440 °FAverage value: 210 °C Grade Count:8
Nozzle Temperature 200 - 227 °C392 - 440 °FAverage value: 218 °C Grade Count:65
Melt Temperature 170 - 279 °C338 - 534 °FAverage value: 220 °C Grade Count:179
Mold Temperature 10.0 - 80.0 °C50.0 - 176 °FAverage value: 48.3 °C Grade Count:184
Drying Temperature 51.7 - 100 °C125 - 212 °FAverage value: 75.3 °C Grade Count:141
Dry Time 1.00 - 4.00 hour1.00 - 4.00 hourAverage value: 2.55 hour Grade Count:140
 2.00 - 4.00 hour
@Temperature 71.1 - 71.1 °C		2.00 - 4.00 hour
@Temperature 160 - 160 °F		Average value: 3.00 hour Grade Count:1
Moisture Content 0.0100 - 0.100 %0.0100 - 0.100 %Average value: 0.0515 % Grade Count:60
Injection Pressure 2.76 - 120 MPa400 - 17400 psiAverage value: 55.0 MPa Grade Count:157
Hold Pressure 2.07 - 8.27 MPa300 - 1200 psiAverage value: 5.14 MPa Grade Count:52
Back Pressure 0.345 - 2.00 MPa50.0 - 290 psiAverage value: 1.07 MPa Grade Count:115
Clamp Pressure 27.6 - 34.5 MPa4000 - 5000 psiAverage value: 31.0 MPa Grade Count:3

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-30767.html

免责声明: 本文 Overview of materials for Polypropylene with 20% Talc Filler 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4